Enhancement of high temperature performance of cement blocks via CO2 curing

Carbonation for the curing of cement-based materials has been gaining increased attention in recent years, especially in light of emerging initiatives to reduce carbon dioxide (CO2) emissions. Carbonation method or CO2 curing is founded on the basis of the reaction between CO2 and cement products to form thermally stable and denser carbonate, which not only improves the physical and mechanical properties of cement-based materials, but also has the ability to utilize and store CO2 safely and permanently. This study aims to assess the effect of CO2 curing technology on the high-temperatures performance of cement blocks. Upon molding, dry-mix cement blocks were cured under statically accelerated carbonation condition (20% CO2 concentration with 70% relative humidity) for 28 days, followed by exposure to elevated temperatures of 300 °C to 800 °C in order to comprehensively study the principal phase changes and decompositions of cement hydrates. The results indicated that CO2 curing improved the performance of cement blocks, such as enhancement in the residual compressive strength and reducing the sorptivity. At 600 °C, the scanning electron microscopy (SEM) revealed a denser microstructure while thermal analisis and X-ray diffraction (XRD) analysis also clearly demonstrated that higher amounts of calcium carbonate were present in the cement blocks after CO2 curing, suggesting better high-temperature performance compared to natural cured cement blocks. In general, an improved high-temperature performance, specifically at 600 °C of the dry-mixed cement blocks was demonstrated by adopting the CO2 curing technology. This confirms the potential of utilizing CO2 curing technology in not only improving quality of cement blocks, new avenue for storing of CO2 in construction material can be realized at the same time.