Ni3A1 is an intermetallic compound which has unique property with temperature. Annealing is done at temperature 300, 500, and 700°C for 1 hour and analyzed with X-ray Diffraction (XRD) and Energy Dispersive X-ray (EDX) analysis for their crystallographic nature. EDX confirmed the composition of Ni3A1 with exact stoichiometry, whereas the XRD confirmed the crystallographic nature of the material. The mechanical properties by hardness results showed that Ni3A1 has highest Vickers hardness value of 554 HV when it is non-heat treated. Its hardness drops as it undergoes annealing process. Corrosion analysis by tafel test shows that its polarization resistance may increase up to 4145 W cm2 when annealed at high temperature. These results show that Ni3A1 is a promising material to be considered as an alternative automotive body.