MATERIAL AND METHODS: The materials were divided into two groups, Fuji IX GIC® (n = 30) and Cention N® (n = 30) and further divided (n = 10) to test three parameters, the fluoride releasing ability, flexural strength, and shear bond strength. Fluoride release was checked using fluoride ion-selective electrode, and flexural strength and shear bond strength were tested using universal testing machine (Intron 3366, UK).
RESULTS: Fluoride release of Fuji IX GIC® was significantly higher compared to that of control Cention N® over a period of 21 days. Flexural strength of Cention N® was significantly higher compared to Fuji IX GIC® and there were no significant differences in shear bond strength of both the materials.
CONCLUSION: From the results of the study, it can be concluded that Cention N® is an alkasite filling material for the complete and permanent replacement of tooth structure in posterior teeth and can be a good alternative when compared to GICs on the basis of their superior mechanical properties.
CLINICAL SIGNIFICANCE: Cention N® is an innovative filling material for the complete and permanent replacement of tooth structure in posterior teeth and can be a good alternative when compared to GICs on the basis of their superior mechanical properties.
METHODS: PubMed and Science Direct were searched for papers published between the years 1974 and 2018. The search was restricted to articles written in English related to modification of glass ionomer cements. Only articles published in peer-reviewed journals were included. The search included literature reviews, in vitro, and in vivo studies. Articles written in other languages, without available abstracts and those related to other field were excluded. About 198 peer-review articles in the English language were reviewed.
CONCLUSION: Based on the finding, most of the modification has improved physical-mechanical properties of glass ionomer cements. Recently, researchers have attempted to improve their antimicrobial properties. However, the attempts were reported to compromise the physical-mechanical properties of modified glass ionomer cements.
CLINICAL SIGNIFICANCE: As the modification of glass ionomer cement with different material improved the physical-mechanical and antimicrobial properties, it could be used as restorative material for wider application in dentistry.
MATERIALS AND METHODS: The HVGICs evaluated were Zirconomer [ZR] (Shofu), Equia Forte [EQ] (GC) and Riva [RV] (SDI). Sixty specimens (12mm x 2mm x 2mm) of each material were fabricated using customized Teflon molds. After initial set, the specimens were removed from their molds, finished, measured and randomly divided into 3 groups of 20. Half the specimens in each group were left uncoated while the remaining half was covered with the respective manufacturers' resin coating. The specimens were subsequently conditioned in distilled water, artificial saliva or citric acid at 37°C for 7 days. The uncoated and coated specimens (n=10) were then subjected to dynamic mechanical testing in flexure mode at 37°C with a frequency of 0.1 to 10Hz. Storage modulus, loss modulus and loss tangent data were subjected to normality testing and statistical analysis using one-way ANOVA/Scheffe's post-hoc test and Ttest at significance level p<0.05.
RESULTS: Mean storage modulus ranged from 1.39 ± 0.36 to 10.80 ± 0.86 GPa while mean loss modulus varied from 0.13 ± 0.03 to 0.70 ± 0.14 GPa after conditioning in the different mediums. Values for loss tangent ranged from 39.4 ± 7.75 to 213.2 ± 20.11 (x10 -3 ). Significant differences in visco-elastic properties were observed between mediums and materials. When conditioned in distilled water and artificial saliva,storage modulus was significantly improved when ZR, EQ and RV were uncoated. Significantly higher values were, however, observed with resin coating when the materials were exposed to citric acid.
CONCLUSION: The visco-elastic properties of HVGICs were influenced by both resin coating and chemical environment.