Purpose of the study: The objective of this study was to investigate the flexural strengths of five commercially available tooth-coloured restorative materials – Alpha-Dent (composite resin, Dental Technologies Inc.), Solare Anterior (composite resin, GC), F2000 (polyacid-modified composite resin, 3M), Beautifil (giomer, Shofu) and Fuji II LC (resin- modified glass ionomer cement, GC] using the ISO 4049 specifications. Materials and Method: Ten specimens of (25±0.2)mm x (2±0.1)mm x (2±0.1)mm from each material were prepared at 22-23ºC using a customized metal mould. After light polymerization, the specimens were stored in distilled water at 37ºC for 24 hours. The specimens were subsequently blotted dry, measured and subjected to flexural testing using an Instron Universal Testing Machine with a crosshead speed of 0.5mm/min. The flexural strengths were calculated from the maximum load exerted on the specimens. Data were analysed using one way ANOVA and scheffe’s post-hoc multiple comparison tests at a significance level of 0.05.Results: The results showed that the mean flexural strengths of Beautifil, Solare Anterior and Alpha-Dent were above 80 MPa and those of F2000 and Fuji II LC were below 80 MPa. The results of one-way ANOVA and Scheffe’s post-host tests demonstrated that Beautifil had significantly higher mean flexural strength compared to Fuji II LC, F2000 and Alpha-Dent (P