CaCu3Ti4O12 (CCTO) has attracted a great attention for electronic devices miniaturization due to its
very high dielectric constant properties at a wide range of frequency and nearly constant over broad temperature range. The origins of the giant dielectric constant have been speculated from electrical heterogeneous of interior elements of the CCTO ceramics. Four origins were suggested contributed to the electrical heterogeneous. In this study heat treatment were done with the electrode contact in Argon gas environment and the electrical properties over very wide frequency of CCTO ceramics were investigated. Cylindrical CCTO pellets samples were prepared by solid state reaction method and single phase of XRD pattern was obtained after sintering processes. Electrical impedance responds were measured at frequency from 100 Hz to 1 GHz for the samples for untreated and heat treated at 200ºC, 250ºC, 300ºC, 350ºC and 400ºC of CCTO. Improvement to the dielectric constant can be seen for 350ºC and 400ºC samples and dielectric loss were improved for 200ºC and 300ºC samples for overall frequency. The variations were discussed based on oxygen deficiency content and resistivity of the elements inside of CCTO structure.
One-dimensional nanostructure materials are very attractive because of their electronic and optical properties depending on their size. It is well known that properties of material can be tuned by reducing size to nanoscale because at the small sizes, that they behave differently with its bulk materials and the band gap will control by the size. The tunability of the band gap makes nanostructured materials useful for many applications. As one of the wide band gaps semiconductor compounds, zinc selenide (ZnSe) nanostructures (nanoparticles, nanowires, nanorods) have received much attention for the application in optoelectronic devices, such as blue laser diode, light emitting diodes, solar cells and IR optical windows. In this study, ZnSe nanostructures have been synthesized by reduction process of zinc selenate using hydrazine hydrate (N2H4.2H2O). The reductive agent of hydrazine hydrate was added to the starting materials of zinc selenate were heat treated at 500 o C for 1 hour under argon flow to form onedimensional nanostructures. The SEM and TEM images show the formation of nanocompositelike structures, which some small nanobars and nanopellets stick to the rod. The x-ray diffraction and elemental composition analysis confirm the formation of mixture zinc oxide and zinc selenide phases.