On-stream inspections are the most appropriate method for routine inspections during plant operation without undergoing production downtime. Ultrasonic inspection, one of the on-stream inspection methods, faces challenges when performed at high temperatures exceeding the recommended 52 °C. This study aims to determine the ultrasonic velocity and attenuation with known material grade, thickness, and temperatures by comparing theoretical calculation and experimentation, with temperatures ranging between 30 °C to 250 °C on low-carbon steel, covering most petrochemical equipment material and working conditions. The aim of the theoretical analysis was to obtain Young's modulus, Poisson's ratio, and longitudinal velocity at different temperatures. The experiments validated the theoretical results of ultrasonic change due to temperature increase. It was found that the difference between the experiments and theoretical calculation is 3% at maximum. The experimental data of velocity and decibel change from the temperature range provide a reference for the future when dealing with unknown materials information on site that requires a quick corrosion status determination.
Petrochemical plants use on-stream inspection often to detect and monitor the corrosion on the equipment and piping system. Compared to ultrasonic thickness gauging and pulse-echo A-scan, phased array corrosion mapping has better coverability and can scan a large area to detect general and localized corrosion. This paper's objective is to obtain documentary evidence for the accuracy of corrosion detection from 30 °C to 250 °C on A36 low-carbon steel by carrying out simulation experiments every 10 °C step. A minimum of three sets of phased array corrosion mapping data in each temperature were collected to study and evaluate the detectability. The data evidence could enhance the confidence level of the plant's end users in using phased array mapping in the future during inspections. The experiments were found to be insufficiently thorough despite addressing the initial concerns, leaving more area for discussion in further studies, such as expanding the investigation to thicker carbon steel, stainless steel, and wedge materials.