An ionic liquid, 1-n-butyl-3-methylimidazolium chloride (BmimCl) was blended with urea at 1:1 mole ratio to create a BmimCl/Urea mixture. The agarose/talc composite films containing the BmimCl/Urea mixture were then acquired through a gelation method. The weight ratio of agarose and talc was fixed at 4:1, while the content of BmimCl/Urea was varied from 0 to 10 wt % relative to the overall weight of the composite films. The tensile stress and modulus results showed the optimum BmimCl/Urea content in the composite film lies at 8 wt %. The talc particles are embedded in the agarose matrix and there are no pullouts for the composite films containing BmimCl/Urea as demonstrated by SEM micrographs. The addition of BmimCl/Urea increased the glass transition temperature of the composite films, however, the thermal decomposition temperature decreased drastically. FTIR and FT-Raman spectra indicated the existence of interaction between agarose and talc, which improves their interfacial adhesion. As a conclusion, a BmimCl/Urea mixture can be utilized as a coupling agent for agarose/talc composite films.
Polybutylene succinate (PBS)/rice starch (RS) blends were prepared via the hot-melt extrusion technique through the usage of a twin-screw extruder without and containing ionic liquid-based surfactants (ILbS). Two types of ILbS were used, specifically, 1-dodecyl-3-methylimidazolium trifluoromethanesulfonate, [C12mim][OTf] and 1-dodecyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, [C12mim][NTf2] were mixed into the PBS/RS blends at the different contents (0-8 wt.%). The tensile and flexural results showed that the blends containing ILbS have a high tensile extension and tensile energy compared to the blend without ILbS. The blends containing ILbS also have a high flexural extension compared with the blend without ILbS. The blends containing [C12mim][NTf2] have a significant improvement in the tensile energy (up to 239%) and flexural extension (up to 17%) in comparison with the blends containing [C12mim][OTf]. The FTIR spectra demonstrated that the presence of ILbS in the blends generated the intermolecular interactions (ion-dipole force and hydrophobic-hydrophobic interaction) between PBS and RS. The DSC results exhibited that the melting points of the prepared blends are decreased with the addition of ILbS. However, the TGA results showed that the thermal decomposition of the blends containing ILbS are higher than the blend without ILbS. The values of decomposition temperature were 387.4 °C, 381.8 °C, and 378.6 °C of PBS/RS-[C12mim][NTf2], PBS/RS-[C12mim][OTf], and PBS/RS, respectively. In conclusion, the ILbS could significantly improve the physicochemical properties of the PBS/RS blends by acting as a compatibilizer.
Biodegradable polymers are an exceptional class of polymers that can be decomposed by bacteria. They have received significant interest from researchers in several fields. Besides this, biodegradable polymers can also be incorporated with fillers to fabricate biodegradable polymer composites. Recently, a variety of ionic liquids have also been applied in the fabrication of the polymer composites. In this brief review, two types of fillers that are utilized for the fabrication of biodegradable polymer composites, specifically organic fillers and inorganic fillers, are described. Three types of synthetic biodegradable polymers that are commonly used in biodegradable polymer composites, namely polylactic acid (PLA), polybutylene succinate (PBS), and polycaprolactone (PCL), are reviewed as well. Additionally, the influence of two types of ionic liquid, namely alkylimidazolium- and alkylphosphonium-based ionic liquids, on the mechanical, thermal, and chemical properties of the polymer composites, is also briefly reviewed. This review may be beneficial in providing insights into polymer composite investigators by enhancing the properties of biodegradable polymer composites via the employment of ionic liquids.