The aim of the present study was to assess the current approaches and philosophies pertaining to direct restorations, bleaching and root canal treatment amongst general dental practitioners (GDPs) in the Klang Valley, Malaysia. A questionnaire, together with a stamped addressed envelope and an explanatory letter, was sent to 200 GDPs in the Klang Valley in April-July 2005. The GDPs were selected at random. A total of 153 (76.5%) of the GDPs responded to the survey. 46.4% of the respondents stated that the use of amalgam was decreasing whereas 79.7% stated an increase in the use of composite resins. Clinical indication (85.6%) and patients’ demand for aesthetics (73.9%) appeared to be the main factors influencing the choice of restorative materials. Fractured restorations was the main reason for the replacement of amalgam restorations (77.1%) whilst secondary caries was the main reason for the replacement of composite resin restorations (73.9%). Almost two thirds of the GDPs surveyed provided chair side bleaching while 75.8% of the GDPs would supervise home bleaching. Sodium hypochlorite was the most common endodontic irrigant used amongst the GDPs surveyed and cold lateral compaction was the most commonly used obturation technique.
Certain beverages e.g. coffee, tea, soft drinks, fruit juices, alcoholic beverages, may affect the physical properties of composite resins. Objectives: The objectives of this study were to: (1) evaluate the effect of different beverages and chilli sauce on the wear resistance of composite resins, (2) evaluate effect of the duration of immersion in the beverages and chilli sauce on the wear resistance of composite resins.
Materials and methods: Disc specimens were fabricated using two different types of composite resins: (i) Filtek Z350 (3M ESPE, USA, nano-filled composite, 40 specimens) and (ii) Solare P (GC Dental Products Corp, Japan, microhybrid composite, 40 specimens). After polymerization, all the specimens were polished using Enhance Polishing System (Dentsply International Inc.,USA). The specimens were air-dried before weighing using Sartorius BP 221S weighing balance (Sartorius AG, Goettingen, Germany). Ten specimens from each type of composite were immersed in distilled water (control group), Coca cola®, orange juice (Peel Fresh®) and chilli sauce (Maggi®) respectively. The duration of immersion was 6 hours and 1 week. A reciprocal compression-sliding system was used to evaluate the wear resistance of the specimens. The specimens were moved back and forth with a loaded counter-body (235g) against sand paper (P1000, 3M ESPE, USA) in running water. The weight of the specimens were measured after 6 hours of immersion and 20,000 wear cycles and also at 1 week of immersion with further 20,000 wear cycles. The wear resistances were tabulated as percentage of weight loss from the specimens. Results were statistically analyzed using one way ANOVA and post-hoc Tukey’s test (p= 0.05).
Results: The results showed that Solare P has significantly lower wear resistance compared to Filtek Z350. There was no significant difference in wear resistance for Filtek Z350 when immersed in chili sauce, Coca-cola® and orange juice in comparison with control group for 6 hours and 1 week. Similar findings were observed for Solare P.
Conclusion: Within the limitations of this study, it was concluded that Solare P has poorer wear resistance than Filtek Z350. The soaking medium investigated and duration of immersion have no influence on the wear resistance of Solare P and Filtek Z350.