  1. Naauman Z, Rajion ZAB, Maliha S, Hariy P, Muhammad QS, Noor HAR
    Eur J Dent, 2019 Feb;13(1):114-118.
    PMID: 31170762 DOI: 10.1055/s-0039-1688741
    OBJECTIVE: The carbon, titanium, and oxygen levels on titanium implant surfaces with or without ultraviolet (UV) pretreatment were evaluated at different wavelengths through X-ray photoelectron spectroscopy (XPS).

    MATERIALS AND METHODS: This interventional experimental study was conducted on nine Dio UFII implants with hybrid sandblasted and acid-etched (SLA) surface treatments, divided equally into three groups. Control group A samples were not given UV irradiation, while groups B and C samples were given UVA (382 nm, 25 mWcm2) and UVC (260 nm, 15 mWcm2) irradiation, respectively. The atomic ratio of carbon, titanium, and oxygen was compared through XPS.

    RESULTS: Mean carbon-to-titanium ratio and C1 peaks considerably increased in Group A compared to those in experimental Groups B and C. The intensity of Ti2p and O1s peaks was more pronounced for group C compared to that for groups A and B.

    CONCLUSIONS: Although the decrease in surface hydrocarbons was the same in both UV-treated groups, the peak intensity of oxygen increased in the UVC-treated group. Thus, it can be concluded that compared with UVA irradiation, UVC irradiation has the potential to induce more hydrophilicity on SLA-coated implants.