In the electrodeposition system, adding saccharin alters the properties of the metal deposits by changing the electrode kinetics of the deposited surface. In this study, nanocrystalline cobalt-iron (CoFe) coating was synthesised using the electrodeposition technique with different saccharin concentrations. The results obtained showed that the coating thickness increased while the grain size decreased from 51 nm to 40 nm when the saccharin concentration increased from 0 to 2 g/L. The nanocrystalline CoFe coating produced with 2 g/L of saccharin concentration resulted in the smallest particle size of 71.22 nm and the highest microhardness of 251.86 HV. From the salt spray test (24 and 48 hours) it was found that the use of saccharin at higher concentration of 2 g/L improves the corrosion resistance of the nanocrystalline CoFe coating significantly due to the change of surface morphology as well as the decrease in grain size.
Kenaf fibre is one of the natural fibers that has received much attention of many researchers because of its good properties and flexible use. Kenaf fibre composites have been proposed as interior building materials. In this study, the recycling effect on the kenaf PVC wall panel is focused. The main objective of this study is to determine the mechanical properties of different types of kenaf PVC wall panels. The samples were formulated based on the first and third recycling process. The specimens were subjected to several types of tests, namely, tensile, izod impact, flexural and hardness based on ASTM D3039, ASTM D256, ASTM D7264 and ASTM D785, respectively. The results indicate that the mechanical properties of the third recycled kenaf PVC wall panel product is better than the virgin and first recycled specimen. This shows that the recycling process enhances the mechanical properties of the product. On the other hand, the hardness of the specimen decreases after first recycling due to the reheating effect.