The synthesized zeolite NaY from rice husk ash (RHA) and the commercial zeolite NaY both modified with surfactants in amounts equal to 50%, 100% and 200% of their external cation exchange capacity (ECEC) were used to remove chromate and arsenate anions from aqueous solutions. While the unmodified zeolite Y had little or no affinity for the Cr(VI) and As(V) anionic species, the surfactant-modified zeolite Y (SMZY) showed significant ability to remove of these anions from the aqueous solutions. The highest chromates and arsenates adsorption efficiency was observed from solutions of pH values 3 and 8, respectively because of the dominance of the univalent species of both anions. The adsorption equilibrium data were best fitted with the Langmuir isotherm model with the highest removal capacities observed for the SMZY initially prepared considering the hexadecyltrimethyl ammonium (HDTMA) amount equal to the 100% of the ECEC of zeolite Y. Synthesized SMZY remove Cr(VI) and As(V) more than the corresponding commercial one due to its lower silica to alumina ratio. Thus, the HDTMA-covered modified zeolite Y synthesized using RHA can be used to remove Cr(VI) and As(V) from water.
Zeolites P in sodium (NaP) and potassium (KP) forms were used as adsorbents for the removal of calcium (Ca2+) and zinc (Zn2+) cations from aqueous solutions. Zeolite KP was prepared by ion exchange of K+ with Na+ which neutralizes the negative charge of the zeolite P framework structure. The ion exchange capacity of K+ on zeolite NaP was determined through the Freundlich isotherm equilibrium study. Characterization of zeolite KP was determined using infrared spectroscopy and X-ray diffraction (XRD) techniques. From the characterization, the structure of zeolite KP was found to remain stable after the ion exchange process. Zeolites KP and NaP were used for the removal of Ca and Zn from solution. The amount of Ca2+ and Zn2+ in aqueous solution before and after the adsorption by zeolites was analysed using the flame atomic absorption spectroscopy method. The removal of Ca2+ and Zn2+ followed the Freundlich isotherm rather than the Langmuir isotherm model. This result also revealed that zeolite KP adsorbs Ca2+ and Zn2+ more than zeolite NaP and proved that modification of zeolite NaP with potassium leads to an increase in the adsorption efficiency of the zeolite. Therefore, the zeolites NaP and KP can be used for water softening (Ca removal) and reducing water pollution/toxicity (Zn removal).
Chlorhexidine (CHX) is known for its high antibacterial substantivity and is suitable for use to bio-inert medical devices due to its long-term antibacterial efficacy. However, CHX molecules require a crosslinking film to be stably immobilized on bio-inert metal surfaces. Therefore, polydopamine (PDA) was utilized in this study to immobilize CHX on the surface of 316L type stainless steel (SS316L). The SS316L disks were pre-treated, modified with PDA film and immobilized with different concentrations of CHX (10mM-50mM). The disks were then subjected to various surface characterization analyses (ATR-FTIR, XPS, ToF-SIMS, SEM and contact angle measurement) and tested for their cytocompatibility with human skin fibroblast (HSF) cells and antibacterial activity against Escherichia coli and Staphylococcus aureus. The results demonstrated the formation of a thin PDA film on the SS316L surface, which acted as a crosslinking medium between the metal and CHX. CHX was immobilized via a reduction process that covalently linked the CHX molecules with the functional group of PDA. The immobilization of CHX increased the hydrophobicity of the disk surfaces. Despite this property, a low concentration of CHX optimized the viability of HSF cells without disrupting the morphology of adherent cells. The immobilized disks also demonstrated high antibacterial efficacy against both bacteria, even at a low concentration of CHX. This study demonstrates a strong beneficial effect of the crosslinked PDA film in immobilizing CHX on bio-inert metal, and these materials are applicable in medical devices. Specifically, the coating will restrain bacterial proliferation without suffocating nearby tissues.
Known for its high genetic diversity and variation in genotypic presence in different regions of the world, hepatitis C virus (HCV) is estimated to infect about 71 million people globally. Selection of an appropriate therapeutic regimen largely depends on the identification of the genotype responsible for the infection. This systematic review and meta-analysis was conducted to provide a comprehensive view of HCV genotype and subtype distribution in Southeast Asia (SEA). The review was conducted according to the Preferred Reporting Items for Systematic Reviews and Meta-analysis (PRISMA). We searched five databases without year and language restrictions. Data from 90 eligible studies involving 15,089 genotypes and 9,646 subtypes representing 10 SEA countries were analyzed. The pooled estimates showed that genotype 1 (46.8%) [95% CI, 43.2-50.4; I2 = 92.77%; p < 0.001] was the most dominant HCV genotype in the region, followed by genotype 3 (23.1%) [95% CI, 19.4-27.2; I2 = 93.03%; p < 0.001], genotype 6 (16.5%) [95% CI, 13.8-19.6], genotype 2 (4.6%) [95% CI, 3.5-5.9], genotype 4 (1.1%) [95% CI, 0.7-1.5] and genotype 5 (0.8%) [95% CI, 0.4-1.3]. Philippines had the highest prevalence of genotypes 1 and 2. Genotype 6 became more prevalent after year 2000. Over 40 different subtypes were identified, with subtypes 1b (26.3%), 1a (21.3%), and 3a (14.3%) being the most prevalent of all the reported subtypes. Although on a global scale, genotype 6 is considered highly prevalent in SEA, evidence from this study reveals that it is the third most prevalent genotype within the region.