Corrosion caused by sulphate-reducing bacteria (SRB) isolated from seawater nearby to Pasir Gudang has been studied. The test coupon was a AISI 304 stainless steel. Potential and corrosion rate measurements were carried out in various types of culturing solutions, with SRB1, SRB2, combination of SRB1 & SRB2 and without SRBs inoculated (sterilized). From Tafel plots a higher corrosion rate has been found in medium inoculated with SRBs than that of the sterilized medium (control). When SRBs were present in the medium, the Tafel plot shifted towards more negative values (Ecorr was shifted to much less anodic values) and increase in current density compared to that of the sterilized medium (control). Localized corrosion was observed on the metal surface, and it was associated to the SRB activity. X-ray analysis (EDAX) showed that the corrosion product has higher content of sulphur for medium containing SRBs than that of the sterilized medium. X-Ray Diffraction analysis carried out on corrosion products which showed the presence of iron sulphide. This indicates the influence of the presence of SRB in corrosion process.
In the attempt to isolate indigenous marine sulphate-reducing bacteria (SRB) from coastal samples, we obtained some swarm forming bacteria. The isolates were screening using Starkey’s medium and detection of main groups of SRB were carried out using commercially kits (SRB BART kits, Droycon Bioconcepts Inc., Canada). From the growth characteristic, only two isolates were strongly suggested as marine SRB. Based on the 16S rRNA gene sequence analysis these SRB were closely related and could be designated as Desulfovibrio sp. and Citrobacter freundii, with the highest sequence similarity of 98% and 93%, respectively.
Sulphate-reducing bacteria (SRB), implicated in microbiologically influenced corrosion were isolated from the deep subsurface at the vicinity of Pasir Gudang, Johor, Malaysia. Electrochemical impedance spectroscopic (EIS) study was carried out to determine the polarization resistance in various types of culturing solutions, with SRB1, SRB2, combination of SRB1 and SRB2 and without SRBs inoculated (control). EIS results showed that in the presence of SRB1, SRB2 and mixed culture SRB1 and SRB2, polarisation resistance values were 7170, 6370 and 7190 ohms respectively compared to that of control, 92400 ohm. X-ray analysis (EDS) of the specimens indicated high sulphur content in the medium containing SRBs. Localized corrosion was observed on the metal surface which was associated with the SRB activity.
Reduced graphene oxide nanosheet (RGO)/Pt nanocomposite have been successfully prepared through a facile chemical reduction method. The reduction of Pt precursor was carried out using sodium borohydride as the efficient chemical reductant. The morphology of RGO/Pt nanocomposite was investigated using high resolution transmission electron microscopy (HRTEM) and field emission scanning electron microscopy (FESEM). HRTEM analysis showed that platinum nanoparticles were homogenously distributed onto the surface of RGO. The electrochemical study proved that Pt nanoparticles were successfully incorporated onto RGO. Therefore, it can be concluded that the proposed method could provide well-dispersed of Pt nanoparticles onto RGO to form RGO/ Pt nanocomposite.