Dihexyl-sexithiophene (DH6T) was doped with tris (8-hydroxyquinolinate) aluminum (Alq3) to prepare blends of DH6T/ Alq3 by dissolving the mixture in the chloroform/hexane co-solvent. Solid films with different thickness deposited on quartz substrates were obtained from the blends via casting process. Optical absorption spectroscopy has been performed to measure the optical band gap of pure and doped DH6T as well as variations in the band gap with dopant concentration (weight %). This variation in optical band gap with dopant concentration was determined quantitatively with fitted and extrapolated techniques and observed qualitatively from the red shift appeared along the optical absorption spectra. The results showed that within a specific dopant content, the optical energy gap, Eg of DH6T decreases from 2.69 eV to 1.8 eV with increasing dopant concentration to 23.1%.
In this research we investigated the effect of composition on the fabrication and morphological characteristics of a hybrid polymeric solar cell which consists of an electron donating conjugated polymer, namely is poly(3-hexylthiophene) (P3HT) combined with an electron-accepting component, which is a type of inorganic compound of TiO2 nanocrystals. The composition of TiO2 in the blends is varied and the optimum performance of the devices are studied. The optical and morphological characterizations are carried out via UV-Visible absorption spectroscopy, X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). The electrical characteristics of the devices are measured by using Keithley 2400 SMU and solar simulator with light intensity of 100 mW/cm2.
In this paper, fabrication and investigation of organic pressure sensor based on AlICIVT-VO 2(3j7)ICu composite is reported. The active layer of the composite was deposited by drop-casting of the blend CN'T-VO 2 (3fl) on a glass substrate (with prefabricated copper (Cu) electrode). The thin film of the blend consists of carbon nanotube CNT, (2.55 wt. %) and vanadium oxide (VO 2 (3fl)) micropowder, (3 wt. %) in benzol (1 mL). The thickness of the composite was in the range of 20-40 ,um. It was found that the fabricated sensor was sensitive to pressure and showed good repeatability. The decrease in resistance of the sensor was observed by increasing the external uniaxial pressure up to 50 kNm-2 . The experimentally obtained results were compared with the simulated results and showed reasonable agreement with each other.