In this study, dynamic vulcanization process was used to improve the thermal properties of calcium carbonate filled composites. The composites were prepared using a Z-blade mixer at 180oC and rotor speed 50rpm. Thermogravimetric analysis (TGA) and Differential scanning calorimetry (DSC) techniques were used to analyze the thermal properties of the composites. The vulcanized and unvulcanized PP/EPDM composites were filled by CaCO3 at 0, 10, 20, 30, and 40 %wt. Meanwhile, thermogravimetric analysis indicates that the total weight loss of PP/EPDM/CaCO3 composites decreased with increasing filler loading. Dynamic vulcanized composites have higher thermal stability, while the crystallinity of PP/EPDM/CaCO3 composites were increased as compared to unvulcanized composites. Therefore, the thermal properties were improved by the presence of
dynamic vulcanization process.
The effect of polypropylene maleic anhydride (PPMAH) on tensile properties and morphology of polypropylene (PP)/recycled acrylonitrile butadiene rubber (NBRr)/ rice husk powder (RHP) composites has been studied. The composites were prepared through melt mixing at 180ºC for 9 minutes using 50 rpm rotor speed. The specimens were analyzed using different techniques, namely tensile test and Scanning Electron Microscopy (SEM). The results obtained showed that the tensile strength and Young’s modulus of the modified composites were increased, while the elongation at break showed the opposite trend as compared with the unmodified composites. The morphology results support the tensile properties and these indicated a better interaction between the filler and matrix with the presence of PPMAH as a compatibilizer.
A chemical modifier (acrylic acid) was used to improve the thermal properties of polypropylene/ ethylene propylene diene terpolymer/calcium carbonate (PP/EPDM/CaCO3) composites. Treated
and untreated PP/EPDM composites were filled by CaCO3 at 0, 20 and 40% wt. The composites
were prepared using Z-blade mixer machine at 180oC and 50 rpm of rotor speed. Thermogravimetric
analysis (TGA) and differential scanning calorimetry (DSC) methods were used to analyze the thermal properties of the composites. Thermogravimetric analysis indicated that the total weight loss of PP/EPDM/CaCO3 composites decreased with the increasing filler loading for the treated and untreated composites. Meanwhile, the presence of acrylic acid was found to have increased the thermal stability and crystallinity of PP/EPDM/CaCO3
.
Fly ash is the finely divided mineral residue resulting from the combustion of coal in electric generating plants. Fly ash consists of inorganic, incombustible matter present in the coal that has been fused during combustion into a glassy, amorphous structure. Fly ash particles are generally spherical in shape and range in size from 2 μm to 10 μm. They consist mostly of silicon dioxide (SiO2), aluminium oxide (Al2O3) and iron oxide (Fe2O3). Fly ash like soil contains trace concentrations of the following heavy metals: nickel, vanadium, cadmium, barium, chromium, copper, molybdenum, zinc and lead. The chemical compositions of the sample have been examined and the fly ash are of ASTM C618 Class F.
Batu Reput’ is primary sediment mineral and abundantly found in Perlis. Perlis is one of the major producers of ‘Batu Reput’ in Malaysia that content large deposit of high-purity dolomite [CaMg (CO3)2]. Pure samples of ‘Batu Reput’ recently explored in the Koperasi Rimba Mas Padang Besar Quarry were investigated for their physical, chemical and mineralogical composition. SEM and XRD analysis methods were applied. The potential of ‘Batu Reput’ as a raw material in fertilizer production was investigated in this paper.