The influence of SiO2/TiO2 nanocomposites (STNCs) content on non-radiative energy transfer (Förster-type) from poly (9,9'-dioctylfluorene-2,7-diyl) (PFO) to poly [2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) using steady-state and time-resolved photoluminescence spectroscopies was investigated at room temperature. The improved energy transfer from PFO to MEH-PPV upon an increment of the STNCs was achieved by examining absorbance, emission (PL) and photoluminescence excitation (PLE) spectra. The shorter values of the quantum yield (φDA) and lifetime (τDA) of the PFO in the hybrid thin films compared with the pure PFO, indicating efficient energy transfer from PFO to MEH-PPV with the increment of STNCs in the hybrid. The energy transfer parameters can be tuned by increment of the STNCs in the hybrid of PFO/MEH-PPV. The Stern-Volmer value (kSV), quenching rate value (kq), Förster radius (R0), distance between the molecules of PFO and MEH-PPV (RDA), energy transfer lifetime (τET), energy transfer rate (kET), total decay rate of the donor (TDR), critical concentration (Ao), and conjugation length (Aπ) were calculated. The gradually increasing donor lifetime and decreasing acceptor lifetime, upon increasing the STNCs content, prove the increase in conjugation length and meanwhile enhance in the energy transfer.
Tuning the emission spectrum of both binary hybrids of poly (9,9'-di-n-octylfluorenyl-2,7-diyl) (PFO) with each poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) and poly[2-methoxy-5-(3,7-dimethyl-octyloxy)-1,4-phenylenevinylene] end-capped with Dimethyl phenyl (MDMO-PPV-DMP) by a systematic doping strategy was achieved. Both binary hybrid thin films of PFO/MEH-PPV and PFO/MDMO-PPV-DMP with various weight ratios were prepared via solution blending method prior to spin coating onto the glass substrates. The conjugation length of the PFO was tuned upon addition of acceptors (MEH-PPV or MDMO-PPV-DMP), as proved from shifting the emission and absorption peaks of the binary hybrids toward the acceptor in addition to enhancing the acceptor emission and reducing the absorbance of the PFO. Förster resonance energy transfer (FRET) is more efficient in the binary hybrid of PFO/MDMO-PPV-DMP than in the PFO/MEH-PPV. The efficient FRET in both hybrid thin films played the major role for controlling their emission and producing white emission from optimum ratio of both binary hybrids. Moreover, the tuning of the emission color can be attributed to the cascade of energy transfer from PFO to MEH-PPV, and then to MDMO-PPV-DMP.