Displaying publications 101 - 120 of 308 in total

Abstract:
Sort:
  1. Fulltext Assessments of Secondary Reinforcement of Epoxy Matrix-Glass Fibre Composite Laminates through Nanosilica (SiO₂)
    Lazar PJL, Sengottuvelu R, Natarajan E
    Materials (Basel), 2018 Nov 05;11(11).
    PMID: 30400592 DOI: 10.3390/ma11112186
    The principal objective of this research work was to investigate the results of impregnating epoxy matrix-glass fibre composite laminates with nanosilica as secondary reinforcement. 0.5, 0.75, 1 and 3 wt% nanosilica was used and thereafter properties of composites were assessed through tensile, three point bending, quasi static indentation tests and dynamic mechanical analysis. Scanning electron microscope examinations were done on fracture surfaces and failure modes were analyzed. The internal failures of the composite due to quasi-static indentation were evaluated through C-Scan. Among samples of different weight fractions, 0.75 wt% nanosilica reinforced composite laminates exhibited substantial increase of 42% in tensile strength and 39.46% in flexural strength. The reduction in glass transition temperature (Tg), increase in storage modulus (E'), loss modulus (E″) and damping factor (tan δ) were also observed. Quasi-static indentation assessments revealed that energy absorption property was enhanced significantly by 53.97%. Hence nanosilica up to 0.75 wt% can be used as a potential candidate for secondary reinforcement in epoxy composite laminates.
    Matched MeSH terms: Tensile Strength
  2. Fulltext Properties and Characterization of a PLA-Chitin-Starch Biodegradable Polymer Composite
    Olaiya NG, Surya I, Oke PK, Rizal S, Sadiku ER, Ray SS, et al.
    Polymers (Basel), 2019 Oct 11;11(10).
    PMID: 31614623 DOI: 10.3390/polym11101656
    This paper presents a comparison on the effects of blending chitin and/or starch with poly(lactic acid) (PLA). Three sets of composites (PLA-chitin, PLA-starch and PLA-chitin-starch) with 92%, 94%, 96% and 98% PLA by weight were prepared. The percentage weight (wt.%) amount of the chitin and starch incorporated ranges from 2% to 8%. The mechanical, dynamic mechanical, thermal and microstructural properties were analyzed. The results from the tensile strength, yield strength, Young's modulus, and impact showed that the PLA-chitin-starch blend has the best mechanical properties compared to PLA-chitin and PLA-starch blends. The dynamic mechanical analysis result shows a better damping property for PLA-chitin than PLA-chitin-starch and PLA-starch. On the other hand, the thermal property analysis from thermogravimetry analysis (TGA) shows no significant improvement in a specific order, but the glass transition temperature of the composite increased compared to that of neat PLA. However, the degradation process was found to start with PLA-chitin for all composites, which suggests an improvement in PLA degradation. Significantly, the morphological analysis revealed a uniform mix with an obvious blend network in the three composites. Interestingly, the network was more significant in the PLA-chitin-starch blend, which may be responsible for its significantly enhanced mechanical properties compared with PLA-chitin and PLA-starch samples.
    Matched MeSH terms: Tensile Strength
  3. Fulltext Polypropylene/Graphene Nanocomposites: Effects of GNP Loading and Compatibilizers on the Mechanical and Thermal Properties
    Al-Saleh MA, Yussuf AA, Al-Enezi S, Kazemi R, Wahit MU, Al-Shammari T, et al.
    Materials (Basel), 2019 Nov 27;12(23).
    PMID: 31783544 DOI: 10.3390/ma12233924
    In this research work, graphene nanoplatelets (GNP) were selected as alternative reinforcing nanofillers to enhance the properties of polypropylene (PP) using different compatibilizers called polypropylene grafted maleic anhydride (PP-g-MA) and ethylene-octene elastomer grafted maleic anhydride (POE-g-MA). A twin screw extruder was used to compound PP, GNP, and either the PP-g-MA or POE-g-MA compatibilizer. The effect of GNP loading on mechanical and thermal properties of neat PP was investigated. Furthermore, the influence and performance of different compatibilizers on the final properties, such as mechanical and thermal, were discussed and reported. Tensile, flexural, impact, melting temperature, crystallization temperature, and thermal stability were evaluated by using a universal testing system, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). For mechanical properties, it was found that increasing GNP content from 1 wt.% to 5 wt.% increased tensile strength of the neat PP up to 4 MPa. The influence of compatibilizers on the mechanical properties had been discussed and reported. For instance, the addition of PP-g-MA compatibilizer improved tensile strength of neat PP with GNP loading. However, the addition of compatibilizer POE-g-MA slightly decreased the tensile strength of neat PP. A similar trend of behavior was observed for flexural strength. For thermal properties, it was found that both GNP loading and compatibilizers have no significant influence on both crystallization and melting temperature of neat PP. For thermal stability, however, it was found that increasing the GNP loading had a significant influence on improving the thermal behavior of neat PP. Furthermore, the addition of compatibilizers into the PP/GNP nanocomposite had slightly improved the thermal stability of neat PP.
    Matched MeSH terms: Tensile Strength
  4. Kesan Komposisi Gentian dan Kaedah Pemprosesan ke atas Sifat Mekanik Komposit NR/LLDPE diperkuat Twaron (Effect of Fiber Composition and Processing Methods on the Mechanical Properties of Twaron Reinforced NR/LLDPE Composites)
    Ishak Ahmad, Mohd Khairil Saat, Ibrahim Abdullah, Azizah Baharum
    Sains Malaysiana, 2004;33.
    Blends of fibre-reinforced rubber based on natural rubber-thermoplastic (NR/LLDPE) reinforced by aramid fibre have been done using melt blending process. Two different processing methods were used; internal mixer and extrusion compounding in twin screw extruder. Twaron loading in the system was varied from 0 to 30%. It was found that increasing the amount of aramid fibre led to an increase in the tensile strength, tensile modulus and hardness of the composites while the strain decreased rapidly. The results showed that the optimum composition of filler loading in NR/LLDPE blend is 20%. The ,echanical behaviour was caused by the strong Twaron-matrices interaction in the composites and effective stress concentrating function of Twaron. Composites prepared using the twin-screw extruder have a higher tensile strength and tensile using the twin-screw extruder have a higher tensile stength and tensile modulus but lower impact strength compared to those prepared using internal mixer. Study of the fracture surface by scanning electron microscopy showed that the composite prepared using the internal mixer produced random fiber orientation while the twin-screw extruder produced the fibers aligned to the longitudinal direction. The results indicate that the mechanical properties of the composite were significantly influenced by the processing technique.
    Penyediaan komposit getah asli termoplastik daripada NR/LLDPE yang diperkuat gentian Twaron telah dijalankan melalui proses adunan leburan. Dua kaedah penyediaan yang berbeza digunakan iaitu menggunakan mesin pencampur dalaman manakala kaedah kedua menggunakan pengekstrud skru kembar. Kandungan Twaron di dalam komposit telah diubah daripada 0 hingga 30%. Keputusan menunjukkan bahawa penambahan Twaron telah meningkatkan nilai tegasan maksima, modulus Young dan kekuatan hentaman komposit tetapi menurunkan nilai terikan maksima. Kandungan Twaron yang optimum adalah 20%. Kehadiran Twaron telah membentuk satu jaringan saling tindak gentian-matriks menyebabkan kekuatan regangan komposit meningkat. Twaron juga berfungsi sebagai penyerap hentaman yang berkesan. Penyediaan komposit menggunakan pengekstrud skru berkembar telah menghasilkan nilai kekuatan regangan yang lebih tinggi berbanding penggunaan pencampur dalaman sebaliknya kekuatan hentaman yang lebih rendah. Kajian morfologi menggunakan mikroskop imbasan elektron mendapati komposit yang disediakan menggunakan pencampur dalaman menghasilkan gentian dengan orientasi rawak manakala pengekstrud skru kembar menghasilkan orientasi gentian yang selari. Keputusan ini menunjukkan bahawa sifat mekanik komposit NR/LLDPE yang diperkuat Twaron sangat dipengaruhi oleh teknik pemprosesan.
    Matched MeSH terms: Tensile Strength
  5. Tensile properties of vulcanized field natural rubber latex by electron beam
    Chai CK, Md. Soot Ahmad, Wan Manshol W. Zin
    Sains Malaysiana, 2008;37.
    Electron beam vulcanization of natural rubber latex has been developed as an alternative to the conventional sulphur vulcanization method. This study aimed at determining the effect of electron beam dose, beam current and centrifugation to the tensile properties of field natural rubber latex. Irradiation dose and beam current ranged from 50 to 300 kGy and 1 to 15 mA respectively. The determination of tensile properties were done on cast film prepared from irradiated field latex before and after centrifugation. It was found that tensile properties increased with radiation dose but decreased with beam current. Rubber films made from centrifuged irradiated field latex were softer and showed higher tensile strength.
    Matched MeSH terms: Tensile Strength
  6. Mechanical properties of alumina trihydrate filled polypropylene/ethylene propylene diene monomer composites for cable applications
    Reza Hashemi Farzad, Azman Hassan, M. Jawaid, M.A.M. Piah
    Sains Malaysiana, 2013;42:801-810.
    Polymeric materials such as polypropylene (PP), polyethylene (PE) and ethylene propylene diene monomer (EPDM) are widely used as insulators for cable applications. We investigated the effect of alumina trihydrate (ATH) loading on the mechanical properties of PP/EPDM blend. Preliminary study showed that PP/EPDM (60:40) was the optimum composition. ATH filled PP/EPDM composites was prepared by using twin screw extruder. In this study, the tensile properties and hardness of the composites were evaluated. The tensile modulus and hardness increased while elongation at break and tensile strength decreased with increasing ATH content. Scanning electron microscope was used to study the morphology of ATH in PP/EPDM blend.
    Matched MeSH terms: Tensile Strength
  7. Pull-out and tensile strength properties of two selected tropical trees
    Normaniza Osman, Mohamad Nordin Abdullah, Che Hassandi Abdullah
    Sains Malaysiana, 2011;40:1123-1127.
    A bioengineering technique is gradually being used as an alternative for slope stabilisation design. The effect of vegetation on soil strength, particularly in terms of root reinforcement aspects has therefore become a major interest. However, there is a lack of documentation on the root mechanical properties available especially in Malaysia. In this study, both pull-out and tensile strength of two tropical trees namely Leucaena leucocephala and Acacia mangium were investigated on different stem sizes. L. leucocephala performs the higher pullout strength than A. mangium. The results also show that pullout resistance is much affected by the root than the shoot profiles. In terms of tensile strength, the tensile strength decreases with increasing root diameter, implying the finer root diameter contribute to the higher tensile strength. In both parameters, L. leucocephala exhibits the highest value. The study suggests that L. leucocephala has an added value as a good potential slope plant for slope stabilization work as it exhibits outstanding root mechanical properties. Interestingly, the results also showed that the pullout force was much affected by the tensile strength. It can be concluded that some root and shoot properties do have a great impact on root mechanical properties such as tensile and pullout strengths.
    Matched MeSH terms: Tensile Strength
  8. Effects of silica on the formation of epoxidised natural rubber/polyvinyl chloride membrane
    Nazwa Jon, Ibrahim Abdullah, Rizafizah Othaman
    Sains Malaysiana, 2013;42:469-473.
    The presence of pores plays an important role for many membrane processes especially in ultrafiltration and microfiltration. Epoxidised natural rubber (ENR)/polyvinyl chloride (PVC) membranes filled with two types of silica fillers were prepared via simultaneous solvent exchange and evaporation of solvent technique. Two types of silica, i.e. microsilica (microcrystalline
    silica powder) and nanosilica (generated from tetraethoxysilane (TEOS)) were used. The chemical composition, morphology and mechanical stability of the membranes were studied. Both types of silica showed good interaction with the membrane matrix. The formation of pores depended on the size of silica particles added. Microsilica produced large pores while insitu generated nanosilica produced nanosized pores. The mechanical properties of membrane improved with the addition
    of silica. The tensile strength increased from 10.6 MPa to 17.8 MPa and 14.5 MPa for nanosilica and microsilica filled membrane while the tensile modulus increased from 1.6 MPa to 3.8 MPa and 3.4 MPa, respectively. Thus, both types of silica acted as a filler as well as pore forming agent for the ENR/PVC membrane.
    Matched MeSH terms: Tensile Strength
  9. Effect of different drying methods on the morphology, crystallinity, swelling ability and tensile properties of nata de coco
    Norhayati Pa'e, Nur Idayu Abd Hamid, Norzieana Khairuddin, Khairul Azly Zahan, Kok FS, Bazlul Mobin Siddique, et al.
    Sains Malaysiana, 2014;43:767-773.
    Nata de coco or bacterial cellulose produced by Acetobacter xylinum is a unique type of biocellulose. It contains more than 90% of water. Dried nata was preferred compared to wet form since it is more convenient and portable with stable properties. Therefore, drying process is necessary in order to produce dried nata de coco. Drying method is a key factor that influenced the properties of dried nata de coco produced. The aim of this study was to investigate the effect of different drying methods on morphology, crystallinity, swelling ability and tensile strength of dried nata de coco. Nata de coco samples were dried using three physical drying methods such as oven, tray dryer or freeze dryer until it achieved 3-5% moisture content. Obviously, the three drying techniques produced web-like structured nata de coco and quite similar crystallinity which was in range between 87 and 89%. Freeze dried sample showed the largest swelling capacity and tensile strength which was found to be 148 MPa. Different drying method gave different properties of nata de coco. Therefore, the present work proposed the most suitable drying method can be utilized based on the properties of end product needed.
    Matched MeSH terms: Tensile Strength
  10. Mechanical, thermal and chemical resistance of epoxidized natural rubber toughened polylactic acid blends
    Mat Uzir Wahi, Azman Hassan, Akos Noel Ibrahim, Nurhayati Ahmad Zawawi, Kunasegeran K
    Sains Malaysiana, 2015;44:1615-1623.
    Polylactic acid (PLA)/Epoxidized natural rubber (ENR-50) blends were prepared by melt extrusion followed by injection
    molding to fabricate the test samples. The effect of ENR-50 loadings on the morphological, mechanical, chemical
    resistance and water absorption properties of the blends were studied using standard methods. The toughness of the
    blend improved with ENR loading up to 20 wt. % but flexural and tensile strength decreased. The balanced mechanical
    properties were obtained at 20 wt. % ENR-50 loading. SEM showed good distribution and increased ENR particle size
    as ENR content increased from 10 to 30 wt. %. The differential scanning calorimeter (DSC) showed a steady drop in
    crystallization temperature (Tc
    ) as ENR content increases while the glass transition temperature (Tg
    ) remained unchanged.
    Water absorption was observed to increase with ENR loadings. Increase in ENR content was also observed to reduce the
    chemical resistance of the blends.
    Matched MeSH terms: Tensile Strength
  11. Bacterial cellulose film coating as drug delivery system: physicochemical, thermal and drug release properties
    Mohd Cairul Iqbal Mohd Amin, Abadi Gumah Abadi, Naveed Ahmad, Haliza Katas, Jamia Azdina Jamal
    Sains Malaysiana, 2012;41:561-568.
    There has been an increasing interest in the use of natural materials as drug delivery vehicles due to their biodegradability, biocompatibility and ready availability. These properties make bacterial cellulose (BC), from nata de coco, a promising biopolymer for drug delivery applications. The aim of this study was to investigate the film-coating and drug release properties of this biopolymer. Physicochemical, morphological and thermal properties of BC films were studied. Model tablets were film coated with BC, using a spray coating technique, and in vitro drug release studies of these tablets were investigated. It was found that BC exhibited excellent ability to form soft, flexible and foldable films without the addition
    of any plasticizer. They were comparable to Aquacoat ECD (with plasticizer) in tensile strength, percentage elongation and elasticity modulus. Differential scanning calorimetry (DSC) BC showed a high Tg value indicating thermally stability of films. These results suggest that BC can be used as novel aqueous film-coating agent with lower cost and better film forming properties than existing film-coating agents.
    Matched MeSH terms: Tensile Strength
  12. Fulltext Improving Performance of Electrospun Nylon 6,6 Nanofiber Membrane for Produced Water Filtration via Solvent Vapor Treatment
    Abd Halim NS, Wirzal MDH, Bilad MR, Md Nordin NAH, Adi Putra Z, Sambudi NS, et al.
    Polymers (Basel), 2019 Dec 17;11(12).
    PMID: 31861059 DOI: 10.3390/polym11122117
    Electrospun nanofiber membrane (NFM) has a high potential to be applied as a filter for produced water treatment due to its highly porous structure and great permeability. However, it faces fouling issues and has low mechanical properties, which reduces the performance and lifespan of the membrane. NFM has a low integrity and the fine mat easily detaches from the sheet. In this study, nylon 6,6 was selected as the polymer since it offers great hydrophilicity. In order to increase mechanical strength and separation performance of NFM, solvent vapor treatment was implemented where the vapor induces the fusion of fibers. The fabricated nylon 6,6 NFMs were treated with different exposure times of formic acid vapor. Results show that solvent vapor treatment helps to induce the fusion of overlapping fibers. The optimum exposure time for solvent vapor is 5 h to offer full retention of dispersed oil (100% of oil rejection), has 62% higher in tensile strength (1950 MPa) compared to untreated nylon 6,6 NFM (738 MPa), and has the final permeability closest to the untreated nylon 6,6 NFM (733 L/m2.h.bar). It also took more time to get fouled (220 min) compared to untreated NFM (160 min).
    Matched MeSH terms: Tensile Strength
  13. Effects of debinding and sintering atmosphere on properties and corrosion resistance of powder injection molded 316 L - stainless steel
    Raza MR, Sherazi I, Muhammad Aslam, Ahmad F, Abu Bakar Sulong, Muhamad Norhamidi, et al.
    Sains Malaysiana, 2017;46:285-293.
    316L stainless steel is a common biomedical material. Currently, biomedical parts are produced through powder injection molding (PIM). Carbon control is the most critical in PIM. Improper debinding can significantly change the properties of the final product. In this work, thermal debinding and sintering were performed in two different furnaces (i.e. laboratory and commercially available furnaces) to study the mechanical properties and corrosion resistance. Debounded samples were sintered in different atmospheres. The samples sintered in inert gas showed enhanced mechanical properties compared with wrought 316L stainless steel and higher corrosion rate than those sintered in the vacuum furnace. The densification and tensile strength of the hydrogen sintered samples increased up to 3% and 51%, respectively, compared with those of the vacuum-sintered samples. However, the samples sintered in inert gas also exhibited reduced ductility and corrosion resistance. This finding is attributed to the presence of residual carbon in debonded samples during debinding.
    Matched MeSH terms: Tensile Strength
  14. Fulltext Characterization and Performance Evaluation of Cellulose Acetate-Polyurethane Film for Lead II Ion Removal
    Iqhrammullah M, Marlina M, Khalil HPSA, Kurniawan KH, Suyanto H, Hedwig R, et al.
    Polymers (Basel), 2020 Jun 09;12(6).
    PMID: 32526903 DOI: 10.3390/polym12061317
    Global pollution from toxic metal waste has resulted in increased research on toxic metal adsorption. A cellulose acetate-polyurethane (CA-PU) film adsorbent was successfully prepared in this research. The cellulose acetate-polyurethane film adsorbent was prepared with a polycondensation reaction between cellulose acetate and methylene diphenyl diisocyanate. The CA-PU bond formation was confirmed by functional group analysis obtained from Fourier transform infrared (FTIR) spectroscopy. The obtained film was characterized for improved tensile and thermal properties with the addition of methylene diphenyl diisocyanate (MDI). The adsorption ability of the obtained film was evaluated with laser-induced breakdown spectroscopy (LIBS). The best film adsorbent from the LIBS was selected and studied for adsorption isotherm. The FTIR analysis confirmed the formation of the CA-PU bond from the polycondensation between cellulose acetate and the methylene diphenyl diisocyanate. The result showed that the addition of methylene diphenyl diisocyanate (MDI) resulted in the urethane network's growth. The characterization result showed an improvement in the morphology, thermal stability, and tensile strength of the film. The LIBS studies showed improvement in the adsorption of Pb2+ with CA-PU compared with the neat CA. The isotherm studies revealed that Pb2+ adsorption by cellulose acetate-polyurethane film adsorbent was heterogeneously dependent on the Freundlich isotherm model (R2 = 0.97044). Overall, the polycondensation method proposed by this study enhanced the Pb2+ removal, and was comparable to those reported in previous studies.
    Matched MeSH terms: Tensile Strength
  15. Fulltext Mercerization Optimization of Bamboo (Bambusa vulgaris) Fiber-Reinforced Epoxy Composite Structures Using a Box-Behnken Design
    Hassan MZ, Roslan SA, Sapuan SM, Rasid ZA, Mohd Nor AF, Md Daud MY, et al.
    Polymers (Basel), 2020 Jun 17;12(6).
    PMID: 32560539 DOI: 10.3390/polym12061367
    The objective of this research is to optimize the alkaline treatment variables, including sodium hydroxide (NaOH) concentration, soaking, and drying time, that influence the mechanical behavior of bamboo fiber-reinforced epoxy composites. In this study, a Box-Behnken design (BBD) of the response surface methodology (RSM) was employed to design an experiment to investigate the mercerization effect of bamboo fiber-reinforced epoxy composites. The evaluation of predicted tensile strength as a variable parameter of bamboo fiber (Bambusa vulgaris) reinforced epoxy composite structures was determined using analysis of variance (ANOVA) of the quadratic model. In this study, a total of 17 experiment runs were measured and a significant regression for the coefficient between the variables was obtained. Further, the triangular and square core structures made of treated and untreated bamboo fiber-reinforced epoxy composites were tested under compressive loading. It was found that the optimum mercerization condition lies at 5.81 wt.% of the NaOH, after a soaking time of 3.99 h and a drying time of 72 h. This optimum alkaline treatment once again had a great effect on the structures whereby all the treated composite cores with square and triangular structures impressively outperformed the untreated bamboo structures. The treated triangular core of bamboo reinforced composites gave an outstanding performance compared to the treated and untreated square core composite structures for compressive loading and specific energy absorbing capability.
    Matched MeSH terms: Tensile Strength
  16. Fulltext Hot Press as a Sustainable Direct Recycling Technique of Aluminium: Mechanical Properties and Surface Integrity
    Yusuf NK, Lajis MA, Ahmad A
    Materials (Basel), 2017 Aug 03;10(8).
    PMID: 28771207 DOI: 10.3390/ma10080902
    Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (Ts = 430, 480, and 530 °C) and holding times (ts = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at Ts = 530 °C and ts = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.
    Matched MeSH terms: Tensile Strength
  17. Fulltext Effect of Starch Loading on the Thermo-Mechanical and Morphological Properties of Polyurethane Composites
    Gaaz TS, Sulong AB, Ansari MNM, Kadhum AAH, Al-Amiery AA, Nassir MH
    Materials (Basel), 2017 Jul 10;10(7).
    PMID: 28773134 DOI: 10.3390/ma10070777
    The advancements in material science and technology have made polyurethane (PU) one of the most important renewable polymers. Enhancing the physio-chemical and mechanical properties of PU has become the theme of this and many other studies. One of these enhancements was carried out by adding starch to PU to form new renewable materials called polyurethane-starch composites (PUS). In this study, PUS composites are prepared by adding starch at 0.5, 1.0, 1.5, and 2.0 wt.% to a PU matrix. The mechanical, thermal, and morphological properties of PU and PUS composites were investigated. Scanning electron microscope (SEM) images of PU and PUS fractured surfaces show cracks and agglomeration in PUS at 1.5 wt.% starch. The thermo-mechanical properties of the PUS composites were improved as starch content increased to 1.5 wt.% and declined by more starch loading. Despite this reduction, the mechanical properties were still better than that of neat PU. The mechanical strength increased as starch content increased to 1.5 wt.%. The tensile, flexural, and impact strengths of the PUS composites were found to be 9.62 MPa, 126.04 MPa, and 12.87 × 10(-3) J/mm², respectively, at 1.5 wt.% starch. Thermal studies showed that the thermal stability and crystallization temperature of the PUS composites increased compared to that of PU. The loss modulus curves showed that neat PU crystallizes at 124 °C and at 127 °C for PUS-0.5 wt.% and rises with increasing loading from 0.5 to 2 wt.%.
    Matched MeSH terms: Tensile Strength
  18. Oil palm fiber biodegradation: physico-chemical and structural relationships
    Omar FN, Hafid HS, Samsu Baharuddin A, Mohammed MAP, Abdullah J
    Planta, 2017 Sep;246(3):567-577.
    PMID: 28620814 DOI: 10.1007/s00425-017-2717-5
    MAIN CONCLUSION: X-ray microtomography results revealed that delignification process damaged the oil palm fibers, which correlated well with reduction of lignin components and increase of the phenolic content. Biodegradation investigation of natural fibers normally focuses on physico-chemical analysis, with less emphasis on physical aspect like fiber structures affect from microbial activity. In this work, the performance of Pycnoporus sanguineus to delignify oil palm empty fruit bunch fibers through solid-state fermentation utilizing various ratio of POME sludge was reported. In addition to tensile testing, physico-chemical and X-ray microtomography (µ-CT) analyses on the oil palm fibers were conducted to determine the effectiveness of the degradation process. The best ratio of fiber to fungi (60:40) was chosen based on the highest lignin loss and total phenolic content values and further investigation was performed to obtain fermentation kinetics data of both laccase and manganese peroxidase. µ-CT results revealed that delignification process damaged the pre-treated and untreated fibers structure, as evident from volume reduction after degradation process. This is correlated with reduction of lignin component and increase of the phenolic content, as well as lower stress-strain curves of the pre-treated fibers compared to the untreated ones (from tensile testing). It is suggested that P. sanguineus preferred to consume the outer layer of the fiber, before it penetrates through the cellular structure of the inner fiber.
    Matched MeSH terms: Tensile Strength
  19. The Effect of Topical Agents on the Tensile Strength of Absorbable and Non-absorbable Suture Materials-An in Vitro Study
    Alnaqi A, Burhamah W, Al-Sultan AT, Taqi E
    World J Surg, 2023 Feb;47(2):448-454.
    PMID: 36316513 DOI: 10.1007/s00268-022-06788-3
    INTRODUCTION: Topical agents are sometimes applied to surgical wounds after closure; these may include antiseptics or antibiotics. Minimal research has been undertaken to investigate the effect of topical regimens on the tensile strength of suture materials.

    AIM: To investigate the effect of four commonly used wound care regimens on the tensile strength of suture materials.

    METHODS: The failure load of 9 different suture materials was tested using the Instron Electroplus E3000 tensile testing machine (Instron Corporation, Norwood, Massachusetts). Tensile strength was represented as the failure load, measured in Newtons (N), and defined as the maximal load that could be applied across the suture prior to failure. Each suture was tested dry and after immersion in one of 4 products for 7 days and tested on day 7. The immersion agents tested were: sodium chloride 0.9%, MicroSafe® (Sonoma Pharmaceuticals, Petaluma, CA), Aqueous Povidone-iodine 10% solution (Betadine-Mundipharma), and Fucidin ointment.

    RESULTS: Sodium chloride 0.9%, MicroSafe®, Aqueous Povidone-iodine 10%, and Fucidin seem to increase the failure load of most absorbable and non-absorbable sutures. However, the failure load of Polyglactin 910 suture (Surgilactin, coated, violet-Ethicon) is reduced by long-term exposure to either sodium chloride 0.9% or MicroSafe®, while the failure load of the Polydioxanone suture (PDS Plus-Ethicon) is reduced by long-term exposure to MicroSafe® only.

    CONCLUSION: In our experiment, the commonly used wound care products have been shown to alter the tensile strength of suture materials. Further human studies are required to ascertain the clinical validity and applicability of our findings.

    Matched MeSH terms: Tensile Strength
  20. A novel approach to evaluate the mechanical responses of elastin-like bioresorbable poly(glycolide-co-caprolactone) (PGCL) suture
    Low YJ, Kittur MI, Andriyana A, Ang BC, Zainal Abidin NI
    J Mech Behav Biomed Mater, 2023 Apr;140:105723.
    PMID: 36821908 DOI: 10.1016/j.jmbbm.2023.105723
    Poly(glycolide-co-caprolactone) (PGCL) has become a novice to the bioresorbable suture owing to the synergistic properties taken from the homo-polyglycolide (PGA) and polycaprolactone (PCL) such as excellent bioresorption and flexibility. In addition to under conventional monotonic loading, the understanding of mechanical responses of PGCL copolymers under complex loading conditions such as cyclic and stress relaxation is crucial for its application as a surgical suture. Consequently, the present work focuses on evaluating the mechanical responses of PGCL sutures under monotonic, cyclic, and stress relaxation loading conditions. Under monotonic loading, the stress-strain behavior of the PGCL suture was found to be non-linear with noticeable strain-rate dependence. Under cyclic loading, inelastic responses including stress-softening, hysteresis and permanent set were observed. During cyclic loading, both stress-softening and hysteresis were found to increase with the maximum strain. In multi-step stress relaxation, the PGCL sutures were observed to exhibit a strong viscoelastic response. In an attempt to describe the relationship between the stress-relaxation and strain-induced crystallization (SIC) occurring during the loading and relaxation processes, a schematic illustration of the conformational change of polymer chains in PGCL sutures was proposed in this work. Results showed that SIC was dependent on the strain level as well as the loading and relaxation durations. The inelastic phenomena observed in PGCL sutures can be thus correlated to the combined effect of stress relaxation and SIC.
    Matched MeSH terms: Tensile Strength
Related Terms
Filters
Contact Us

Please provide feedback to Administrator ([email protected])