Efforts to reduce manufacturing cost and negative environmental impacts have seen the mixture of natural fibre with synthetic fibre in composite structures. However, there are limited studies on the notch effect and fibre orientation on mechanical properties of hybrid fibre metal laminate (FML). In this study, tensile properties of FML with notch and different fibre orientation were investigated. The hybrid FML incorporated with kenaf fibre at the middle layer was compared with FML with three layers of E-glass fibre. Kenaf fibre and E-glass fibre used were in plain woven form. The FML in 2/1 configuration was manufactured through hot press manufacturing method to bond layers of annealed aluminium 5052 to the composite. Tensile test was conducted in a quasi-static manner according to ASTM E8. The results showed FML with three layers of glass fibre exhibited higher tensile strength compared with hybrid FML. However, the introduction of kenaf fibre in hybrid FML reduces the notch and fibre orientation sensitivity compared with glass fibre reinforced FML.
Pectin bionanocomposite films filled with various concentrations of two different types of halloysite nanotubes were prepared and characterized in this study as potential films for food packaging applications. The two types of halloysite nanotubes were long and thin (patch) (200-30 000 nm length) and short and stubby (Matauri Bay) (50-3000 nm length) with different morphological, physical, and dispersibility properties. Both matrix (pectin) and reinforcer (halloysite nanotubes) used in this study are considered as biocompatible, natural, and low-cost materials. Various characterization tests including Fourier transform infrared spectroscopy, field emission scanning electron microscopy, release kinetics, contact angle, and dynamic mechanical analysis were performed to evaluate the performance of the pectin films. Exceptional thermal, tensile, and contact angle properties have been achieved for films reinforced by patch halloysite nanotubes due to the patchy and lengthy nature of these tubes, which form a bird nest structure in the pectin matrix. Matauri Bay halloysite nanotubes were dispersed uniformly and individually in the matrix in low and even high halloysite nanotube concentrations. Furthermore, salicylic acid as a biocidal agent was encapsulated in the halloysite nanotubes lumen to control its release kinetics. On this basis, halloysite nanotubes/salicylic acid hybrids were dispersed into the pectin matrix to develop functional biofilms with antimicrobial properties that can be extended over time. Results revealed that shorter nanotubes (Matauri Bay) had better ability for the encapsulation of salicylic acid into their lumen, while patchy structure and longer tubes of patch halloysite nanotubes made the encapsulation process more difficult, as they might need more time and energy to be fully loaded by salicylic acid. Moreover, antimicrobial activity of the films against four different strains of Gram-positive and Gram-negative bacteria indicated the effective antimicrobial properties of pectin/halloysite functionalized films and their potential to be used for food packaging applications.
Carbon nanotube reinforced aluminium matrix composites (Al-CNTs) have been widely used in aerospace and automotive industries where high quality and strength is required. The enhanced mechanical properties of Al-CNTs are closely related to processing technique due to challenges within production of these composite materials. In the current review, solid state processing techniques used for synthesizing Al-CNTs have been reviewed to provide an insight into the features and capabilities of each technique regarding the incorporation of CNT reinforcements. To conclude, the mechanical performance of Al-CNT composites is mainly decided by the capability of each technique in the dispersion of CNTs within the aluminum matrix.
The whole Bachok area is covered by alluvial deposit. The alluvium has three aquifers at depth of 0 - 5, 15 - 30 and 40 - 60 meters below surface. Preliminary geophysical surveys including seismic refraction, reflection and resistivity techniques have been carried out to investigate thickness and depth of the aquifers, depth of bedrock and the salinity of the underground water. Results show that the position of first aquifer has been well determined by seismic refraction technique. Whereas the details of deeper aquifers and the bedrock have been determined by seismic reflection techniques. Geoelectrical resistivity low obtained for the first aquifer suggest that it could be due to either salt water intrusion or the presence of marine clay.
Keseluruhan kawasan Bachok merupakan endapan aluvium. Endapan ini mempunyai tiga akuifer pada kedalaman 0 - 5 meter, 15 - 30 meter dan 40 - 60 meter. Kajian geofizik pada tahap awal yang merangkumi aspek seismos biasan, seismos pantulan dan kerintangan geoelektrik telah dilakukan untuk menyiasat ketebalan dan kedalaman akuifer, kedalaman batu dasar dan kemasinan air tanah. Hasil kajian menunjukkan bahawa teknik seismos biasan telah dapat menghasilkan maklumat mengenai kedudukan akuifer pertama. manakala teknik seismos pantulan menghasilkan maklumat terperinci mengenai akuifer kedua dan ketiga serta batu dasar. Nilai kerintangan geoelektrik rendah bagi akuifer pertama menunjukkan sama ada disebabkan oleh intrusi air masin atau kehadiran lempung samudera.
The sorption parameters of two heavy metals (i.e. Pb and Cu) in clay soils from Selangor were studied using batch equilibrium test. The test was conducted in two separate systems, i.e. single and mix solutions. The sorption isotherms data from this test were then used to calculate the sorption parameters, i.e. distribution coefficient (Kd) and maximum adsorption capacity (Am). Langmuir sorption equation was used to model the sorption data with the correlation coefficients (r2) higher than 0.6. The study has revealed that different soils have different sorption capacity for different heavy metals. The Kd values are proportional to the sorption capacity of the soils. The sorption of Pb and Cu in single solution is higher than in mix solution, due to the competition for sorption sites among heavy metals in mix solution. The Kd values for Pb in single solution ranging from 36.18-334.48 L/g and for Cu is 9.29-66.19 L/g. In mix solution, the Kd values for Pb and Cu are much smaller, ranging from 23.13-31.79 L/g and 3.95-18.53 L/g respectively. The Am values in single solution for both Pb and Cu are ranging from 0.48-1.09 mg/g dan 0.18-0.70 mg/g respectively. While in mix solution, the values of Am for Pb ranging from 0.20-1.11 mg/g and Cu within 0.18-0.60 mg/g.
Kajian kepekatan logam dalam air di Tasik Bukit Merah telah dijalankan pada April 2009. Lima belas stesen persampelan telah dipilih dan sampel air permukaan bagi penentuan logam telah diambil. Beberapa parameter kualiti air seperti suhu, konduktiviti, oksigen terlarut, pH dan keliatan air telah ditentukan di setiap stesen. Sebanyak 11 jenis logam iaitu kadmium, zink, plumbum, kuprum, nikel, ferum, kobalt, aluminium, barium, kromium dan mangan (Mn) telah ditentukan dalam sampel air. Keputusan menunjukkan kepekatan semua logam kajian berada di bawah kepekatan maksimum yang dicadangkan oleh piawaian Malaysia dan antarabangsa bagi melindungi hidupan akuatik kecuali bagi logam Fe dan Al. Bagi parameter kualiti air, kajian menunjukkan semua parameter berada dalam julat kepekatan semula jadi (kelas I) berdasarkan Piawaian Kualiti Air Kebangsaan (NWQS Malaysia) kecuali oksigen terlarut dan pH di beberapa stesen persampelan terutama di bahagian timur tasik yang didapati dipengaruhi oleh faktor-faktor semula jadi dan antropogenik.
The formation of nano pores on aluminum at 30oC- 38oC, employing a one step anodization technique which does not require removing the oxide layer formed is presented. A 20% phosphoric acid electrolyte (concentration higher than the normal anodization concentration of 5 to 10%) at a cell potential of 60 volts was used. A platinum electrode was used as the cathode electrode while the aluminum substrate as the anode electrode. A dc powered electrochemical cell to provide the required amount of current density (without the use of temperature controlled water bath) suitable or necessary for pore formation at room temperature was employed. The results obtained show that pore formation at room temperature is achievable and the pore diameter ranged between 80-120 nm.
It is well-known that the characteristics of hardness and drillability are influenced by microstructure of rock. In this study, rock properties were analyzed on grain size and grain content. Coarse-grain and fine-grain sandstones were tested under successive indentation condition. Eighteen groups of sandstone and shale were employed for the drillability test. Indentation tests results showed that grain size influenced the low point of residual hardness, the crushing depth and volume and grain content influenced the peak point of hardness. The drillability values of shale increased with increasing contents of clay and quartz. Meanwhile, drillability values of sandstone increased with increasing content of quartz, but decreased with increasing content of clay. Therefore, these preliminary studies show great potential applications for selecting suitable bit type and formulating drilling program as a function of rock microstructure and crushing rock method for bit in the oil drilling.
Metallic foams are a new class of materials that have a great potential to be used in various functional and structural applications. Due to their competitive price compared to aluminium, metallic foams are anticipated to become an alternative material for light-weight structures. In this study, stainless steel foams are fabricated using a powder space holder method. The materials used include stainless steel powder, a novel space holder glycine and binders consisting of palm stearin and of polyethylene (PE). The stainless steel foams are sintered at 1100o C, 1200o C and 1300o C with sintering times of 1, 2 and 3 h, respectively, to investigate the effects of the sintering parameters on the compressive yield strength of the stainless steel foams. The results showed that all of the stainless steel foams produced exhibit the general behaviours of metal foams. The sintering time is the most significant parameter that influences the compressive yield strength of stainless steel foams. Increasing the sintering temperature and sintering time will increase the compressive yield strength. The interaction between the sintering temperature and sintering time is found to be not statistically significant.
Ground improvement using artificial crust composite foundation, consisting of stabilization of soft clay and composite foundation, is an effective technique for the treatment of deep soft soil layers under infrastructure embankments. In this study, the load responses and settlement performance of this improvement technique were investigated using two centrifuge model tests to compare the variations of the vertical deformation, pore water pressure, axial force of the piles and tensile stress at the bottom of the artificial crust in the crust composite foundation with those in pile-supported embankment. The results of centrifuge model tests showed that the load responses and settlement performance of artificial crust composite foundation was different from the pile-supported embankment, which displayed mainly that the final middle settlement of crust composite foundation can be reduced by about 15% compared with those of pile-supported embankment with the same length of pile and construction cost. The deformation of the crust with the characteristics of the plate was found based on the change of the tensile stress. Additionally, the excess pore water pressure in the crust composite foundation was lower owing to the stress diffusion effect of the crust during the loading period and the dissipation rate of excess pore water pressure was slower due to lower permeability of the crust at the same loading period. Eventually, the axial force of the middle piles was reduced. At the same time, the boundary stress was functioned with the crust, the axial force of the side piles was improved. The comparison of measured and calculated results was carried out using the stress reduction ratio, the result shows that the bearing capacity of the subsoil in the crust composite was improved.
This paper investigates the compressibility characteristics of compacted clay treated with cement, peat ash and silica
sand. For this purpose, one dimensional consolidation tests were conducted to determine the soil consolidation properties.
The test specimens were trimmed from the compaction test specimen. The 1D consolidation test specimen was subjected
to the normal pressures of 2.5, 5, 10, 20, 40, 80 and 160 kPa in sequence on the test specimen which was saturated with
distilled water. At the end of the loading period of 80 kPa, the vertical load was removed and the specimen was allowed
to expand for 24 h for the purpose of evaluating of its swelling behavior. The results showed that void ratio of the soil
specimens decreased with increasing effective normal pressure. The laboratory investigation clearly demonstrates that,
settlement is as the compression of a soil specimen due to vertical loading applied at the top surface of the 1D consolidation
test specimen. It was concluded that, the compression settlement of the stabilized soil with the binder composition of
18% cement, 2% peat ash and 5% silica sand improved by almost 1.3-fold. A notable discovery is the suitability of the
stabilized soil for road embankment and low lying marginal area for foundation works; also solving the environmental
problems in relation to peaty ground. However, sufficient laboratory and field testing are required.
Pilot-scale constructed wetlands planted with Scirpus grossus, were used to investigate the effects of applying a three-rhizobacterial consortium (Bacillus cereus strain NII, Bacillus subtilis strain NII and Brevibacterium sp. strain NII) on the growth of S. grossus and also on the accumulation of iron (Fe) and aluminium (Al) in S. grossus. The experiment includes constructed wetlands with the addition of 2% of the consortium rhizobacteria and without the consortium rhizobacteria addition (acting as control). During each sampling day (0, 5, 10, 15, 20, 25, 30, 42, 72 and 102), plant height, concentration of Fe and Al and sand microbial community were investigated. The results for the constructed wetland with the addition of consortium rhizobacteria showed the growth of S. grossus increased significantly at 26% and 29% for plant height and dry weight, respectively. While the accumulation of Fe and Al in S. grossus were enhanced about 48% and 19% respectively. To conclude, the addition of the rhizobacteria consortium has enhanced both the growth of S. grossus and the metal accumulation. These results suggesting that rhizobacteria has good potential to restore Fe and Al contaminated water in general and particularly for mining wastewater.
Halloysite nanotubes (HNTs) have recently been the subject of extensive research as a reinforcing filler. HNT is a natural nanoclay, non-toxic and biocompatible, hence, applicable in biomedical fields. This review focuses on the mechanical, thermal, and functional properties of polymer nanocomposites with HNT as a reinforcing agent from an experimental and theoretical perspective. In addition, this review also highlights the recent applications of polymer/HNT nanocomposites in the biomedical fields.
The evaluation of complex organic and inorganic coagulant's performances and their relationships could compromise the surface water treatment process time and its efficiency. In this work, process optimization was investigated by comparing an eco-friendly chitosan with the industrially used coagulants namely aluminum sulfate (alum), polyaluminum chloride (PAC), and aluminum chlorohydrate (ACH) in compliance with national drinking water standards. To treat various water samples from different treatment plants with turbidity and pH ranges from 20-826.3 NTU and 5.21-6.80, respectively, 5-20 mg/L coagulant dosages were varied in the presence of aluminum, ferum, and manganese. Among all, 10 mg/L of the respective ACH and chitosan demonstrated 97% and 99% turbidity removal in addition to the removal of the metals that complies with the referred standard. However, chitosan owes fewer sensitive responses (turbidity and residual metal) with the change in its input factors (dosage and pH), especially in acidic conditions. This finding suggested its beneficial role to be used under the non-critical dosage monitoring. Meanwhile, ACH was found to perform better than chitosan only at pH > 7.4 with half dosage required. In summary, chitosan and ACH could perform equally at a different set of optimum conditions. This optimization study offers precise selections of coagulants for a practical water treatment operation.
We demonstrate efficient semipolar (11-22) 550 nm yellow/green InGaN light-emitting diodes (LEDs) with In0.03Ga0.97N barriers on low defect density (11-22) GaN/patterned sapphire templates. The In0.03Ga0.97N barriers were clearly identified, and no InGaN clusters were observed by atom probe tomography measurements. The semipolar (11-22) 550 nm InGaN LEDs (0.1 mm2 size) show an output power of 2.4 mW at 100 mA and a peak external quantum efficiency of 1.3% with a low efficiency drop. In addition, the LEDs exhibit a small blue-shift of only 11 nm as injection current increases from 5 to 100 mA. These results suggest the potential to produce high efficiency semipolar InGaN LEDs with long emission wavelength on large-area sapphire substrates with economical feasibility.
The nanomechanical properties of carbon nanotubes particulate-reinforced aluminum matrix nanocomposites (Al-CNTs) have been characterized using nanoindentation. Bulk nanocomposite specimens containing 2 wt % multiwalled CNTs (MWCNTs) were synthesized by a combination of ball milling and powder metallurgy route. It has been tried to understand the correlation between microstructural evolution particularly carbon nanotubes (CNTs) dispersion during milling and mechanical properties of Al-2 wt % nanocomposites. Maximum enhancement of +23% and +44% has been found in Young's modulus and hardness respectively, owing to well homogenous dispersion of CNTs within the aluminum matrix at longer milling time.
In recent years, closed-cell porous Aluminum (Al) has drawn increasing attention, particularly in the applications requiring reduced weight and energy absorption capability such as in the automotive and aerospace industries. In the present work, porous Al with closed-cell structure was successfully fabricated by powder metallurgy technique using PMMA as a space holder. The effects of the amount of PMMA powder on the porosity, density, microstructure and compressive behaviors of the porous specimens were systematically evaluated. The results showed that closed-cell porous Al having different porosities (12%-32%) and densities (1.6478 g/cm³, 1.5125 g/cm³ and 1.305 g/cm³) could be produced by varying the amount of PMMA (20-30 wt %). Meanwhile, the compressive behavior results demonstrated that the plateau stress decreased and the energy absorption capacity increased with increasing amount of PMMA. However, the maximum energy absorption capacity was achieved in the closed-cell porous Al with the addition of 25 wt % PMMA. Therefore, fabrication of closed-cell porous Al using 25 wt % PMMA is considered as the optimal condition in the present study since the resultant closed-cell porous Al possessed good combinations of porosity, density and plateau stress, as well as energy absorption capacity.
A new contactless technique for latent fingerprint visualization on nonporous curved surfaces of circular cross section was introduced by Low et al. (1). The technique utilizes a plane mirror to convey the light rays toward the inspected surfaces for latent fingerprint visualization. This research activity came up as an extension of the previous study which utilized an aluminum plate as the plane mirror to illuminate the inspected surfaces. Dulling spray was used to increase the diffuse component of the reflective aluminum plate. However, the amount of dulling spray will affect the uniformity of the illumination on the inspected curved surfaces. In this study, a study on the new materials for the plane mirror was carried out. Coated aluminum, opal, and ground glass diffusers were selected as the new materials. The performance of the new materials was compared to the aluminum based on the quality of the captured images on various nonporous cylindrical surfaces. A statistical approach known as randomized complete block design was used to design the experiment. The quality of the captured images was obtained using Spectral Image Validation and Verification. Two-way analysis of variance and Fisher's least significant difference test were used to analyze the quality of the images. From the results of the statistical analysis, coated aluminum has the best performance compared to aluminum, opal, and ground glass diffusers.
A D-shaped polarization-maintaining fiber (PMF) as fiber optic sensor for the simultaneous monitoring of strain and the surrounding temperature is presented. A mechanical end and edge polishing system with aluminum oxide polishing film is utilized to perform sequential polishing on one side (lengthwise) of the PMF in order to fabricate a D-shaped cross-section. Experimental results show that the proposed sensor has high sensitivity of 46 pm/µε and 130 pm/°C for strain and temperature, respectively, which is significantly higher than other recently reported work (mainly from 2013) related to fiber optic sensors. The easy fabrication method, high sensitivity, and good linearity make this sensing device applicable in various applications such as health monitoring and spatial analysis of engineering structures.
The effect of room temperature ionic liquid (RTIL) on the formation of the fluorescence ternary complex oxalate-sodium morin-5-sulfonate (NaMSA)-Aluminium(III) has been studied. In weakly acidic medium and in the presence of RTIL, 1-Butyl-3-methylimidazolium hexafluorophosphate (BMIM-PF6), total complex formation is achieved as compared with the formation of the binary complex of NaMSA-Aluminium(III). The fluorescence characteristics of the system allowed the establishment of a very sensitive method for the spectrofluorimetric determination of oxalate ion. The ternary complex formed its highest fluorescence signal at 513 nm and excitation at 420 nm. In these conditions, the method produces a detection limit of 0.57 ng mL(-1). The procedure has been satisfactorily applied to the determination of oxalate ion in a vegetal tissue (spinach leaves).