Arundo donax L. is investigated in this study as a suitable reinforcing agent for PLA/PP waste blend 3D printing filament. To improve the compatibility of the fibre and polymer, the Arundo fibre was chemically modified using alkali and silane treatment. Untreated and treated fibres were extruded with Polymer blends before being 3D printed. Effect of chemical treatment on thermal, mechanical, and morphological properties of the composites was investigated. The tensile, Izod impact, and water absorption of the 3D printed specimens were also tested. The Alkali treated (ALK) and combination of alkali and silane treatment (SLN) composites displayed good results. Tensile strength and modulus of the materials increased, as well as their maintained stability in the Izod impact test, demonstrating that the incorporation of ArF did not result in a loss in performance. SEM examination supported these findings by confirming the creation of beneficial interfacial contacts between the matrix and fibre components, as demonstrated by the lack of void between the matrix and the fibre surface. Furthermore, the alkali treatment of the ArF resulted in a considerable reduction in water absorption inside the biocomposite, with a 64% reduction seen in ALK composite comparison to the untreated composite (Un). After the 43-day assessment period.
In this study, polybutylene succinate (PBS) was blended with five types of modified tapioca starch to investigate the effect of modified tapioca starch in PBS blends for food packaging by identifying its properties. Tensile and flexural properties of blends found deteriorated for insertion of starch. This is due to poor interface, higher void contents and hydrolytic degradation of hydrophilic starch. FTIR results show all starch/PBS blends are found with footprints of starch except OH stretching vibration which is absent in B40 blends. Besides, Broad O⁻H absorption in all specimens show that these are hydrogen bonded molecules and no free O⁻H bonding was found. SEM testing shows good interfacial bonding between PBS and starch except E40 blends. Therefore, poor results of E40 blends was expected. In TGA, a slightly weight loss found between 80 to 100 °C due to free water removal. Apart from this, insertion of all types of starch reduces thermal stability of blend. However, high crystallinity of starch/PBS blend observed better thermal stability but lower char yield. Starch A and B blends are suggested to be used as food wrap and food container materials while starch D blend is suitable for grocery plastic bags according to observed results.
Extraction of lignin via green methods is a crucial step in promoting the bioconversion of lignocellulosic biomasses. In the present study, utilisation of natural deep eutectic solvent for the pretreatment of kenaf fibres biomass is performed. Furthermore, extracted lignin from natural deep eutectic solvent pretreated kenaf biomass was carried out and its comparative study with commercial lignin was studied. The extracted lignin was characterized and investigated through Infrared Fourier transform spectroscopy, X-ray Diffraction, thermogravimetric analysis, UV-Vis spectroscopy, and scanning electron microscopy. FTIR Spectra shows that all samples have almost same set of absorption bands with slight difference in frequencies. CHNS analysis of natural deep eutectic solvent pretreated kenaf fibre showed a slight increase in carbon % from 42.36 to 43.17% and an increase in nitrogen % from - 0.0939 to - 0.1377%. Morphological analysis of commercial lignin shows irregular/uneven surfaces whereas natural deep eutectic solvent extracted lignin shows smooth and wavy surface. EDX analysis indicated noticeable peaks for oxygen and carbon elements which are present in lignocellulosic biomass. Thermal properties showed that lignin is constant at higher temperatures due to more branching and production of extremely condensed aromatic structures. In UV-VIS spectroscopy, commercial lignin shows slightly broad peak between 300 and 400 nm due to presence of carbonyl bond whereas, natural deep eutectic solvent extracted lignin does not show up any peak in this range. XRD results showed that the crystallinity index percentage for kenaf and natural deep eutectic solvent treated kenaf was 70.33 and 69.5% respectively. Therefore, these innovative solvents will undoubtedly have significant impact on the development of clean, green, and sustainable products for biocatalysts, extraction, electrochemistry, adsorption applications.
Nowadays, microbially induced calcium carbonate precipitation (MICP) has received great attention for its potential in construction and geotechnical applications. This technique has been used in biocementation of sand, consolidation of soil, production of self-healing concrete or mortar, and removal of heavy metal ions from water. The products of MICP often have enhanced strength, durability, and self-healing ability. Utilization of the MICP technique can also increase sustainability, especially in the construction industry where a huge portion of the materials used is not sustainable. The presence of bacteria is essential for MICP to occur. Bacteria promote the conversion of suitable compounds into carbonate ions, change the microenvironment to favor precipitation of calcium carbonate, and act as precipitation sites for calcium carbonate crystals. Many bacteria have been discovered and tested for MICP potential. This paper reviews the bacteria used for MICP in some of the most recent studies. Bacteria that can cause MICP include ureolytic bacteria, non-ureolytic bacteria, cyanobacteria, nitrate reducing bacteria, and sulfate reducing bacteria. The most studied bacterium for MICP over the years is Sporosarcina pasteurii. Other bacteria from Bacillus species are also frequently investigated. Several factors that affect MICP performance are bacterial strain, bacterial concentration, nutrient concentration, calcium source concentration, addition of other substances, and methods to distribute bacteria. Several suggestions for future studies such as CO2 sequestration through MICP, cost reduction by using plant or animal wastes as media, and genetic modification of bacteria to enhance MICP have been put forward.
Since ancient Egypt, orthosis was generally made from wood and then later replaced with metal and leather which are either heavy, bulky, or thick decreasing comfort among the wearers. After the age of revolution, the manufacturing of products using plastics and carbon composites started to spread due to its low cost and form-fitting feature whereas carbon composite were due to its high strength/stiffness to weight ratio. Both plastic and carbon composite has been widely applied into medical devices such as the orthosis and prosthesis. However, carbon composite is also quite expensive, making it the less likely material to be used as an Ankle-Foot Orthosis (AFO) material whereas plastics has low strength. Kenaf composite has a high potential in replacing all the current materials due to its flexibility in controlling the strength to weight ratio properties, cost-effectiveness, abundance of raw materials, and biocompatibility. The aim of this review paper is to discuss on the possibility of using kenaf composite as an alternative material to fabricate orthotics and prosthetics. The discussion will be on the development of orthosis since ancient Egypt until current era, the existing AFO materials, the problems caused by these materials, and the possibility of using a Kenaf fiber composite as a replacement of the current materials. The results show that Kenaf composite has the potential to be used for fabricating an AFO due to its tensile strength which is almost similar to polypropylene's (PP) tensile strength, and the cheap raw material compared to other type of materials.
In recent years, there has been considerable interest in the use of natural fibers as potential reinforcing fillers in polymer composites despite their hydrophilicity, which limits their widespread commercial application. The present study explored the fabrication of nanocomposites by melt mixing, using an internal mixer followed by a compression molding technique, and incorporating rice husk (RH) as a renewable natural filler, montmorillonite (MMT) nanoclay as water-resistant reinforcing nanoparticles, and polypropylene-grafted maleic anhydride (PP-g-MAH) as a compatibilizing agent. To correlate the effect of MMT delamination and MMT/RH dispersion in the composites, the mechanical and thermal properties of the composites were studied. XRD analysis revealed delamination of MMT platelets due to an increase in their interlayer spacing, and SEM micrographs indicated improved dispersion of the filler(s) from the use of compatibilizers. The mechanical properties were improved by the incorporation of MMT into the PP/RH system and the reinforcing effect was remarkable as a result of the use of compatibilizing agent. Prolonged water exposure of the prepared samples decreased their tensile and flexural properties. Interestingly, the maximum decrease was observed for PP/RH composites and the minimum was for MMT-reinforced and PP-g-MAH-compatibilized PP/RH composites. DSC results revealed an increase in crystallinity with the addition of filler(s), while the melting and crystallization temperatures remained unaltered. TGA revealed that MMT addition and its delamination in the composite systems improved the thermal stability of the developed nanocomposites. Overall, we conclude that MMT nanoclay is an effective water-resistant reinforcing nanoparticle that enhances the durability, mechanical properties, and thermal stability of composites.
The major hurdle in melt-processing of ultra-high molecular weight polyethylene (UHMWPE) nanocomposite lies on the high melt viscosity of the UHMWPE, which may contribute to poor dispersion and distribution of the nanofiller. In this study, UHMWPE/cellulose nanofiber (UHMWPE/CNF) bionanocomposites were prepared by two different blending methods: (i) melt blending at 150 °C in a triple screw kneading extruder, and (ii) non-melt blending by ethanol mixing at room temperature. Results showed that melt-processing of UHMWPE without CNF (MB-UHMWPE/0) exhibited an increment in yield strength and Young's modulus by 15% and 25%, respectively, compared to the Neat-UHMWPE. Tensile strength was however reduced by almost half. Ethanol mixed sample without CNF (EM-UHMWPE/0) on the other hand showed slight decrement in all mechanical properties tested. At 0.5% CNF inclusion, the mechanical properties of melt-blended bionanocomposites (MB-UHMWPE/0.5) were improved as compared to Neat-UHMWPE. It was also found that the yield strength, elongation at break, Young's modulus, toughness and crystallinity of MB-UHMWPE/0.5 were higher by 28%, 61%, 47%, 45% and 11%, respectively, as compared to the ethanol mixing sample (EM-UHMWPE/0.5). Despite the reduction in tensile strength of MB-UHMWPE/0.5, the value i.e., 28.4 ± 1.0 MPa surpassed the minimum requirement of standard specification for fabricated UHMWPE in surgical implant application. Overall, melt-blending processing is more suitable for the preparation of UHMWPE/CNF bionanocomposites as exhibited by their characteristics presented herein. A better mechanical interlocking between UHMWPE and CNF at high temperature mixing with kneading was evident through FE-SEM observation, explains the higher mechanical properties of MB-UHMWPE/0.5 as compared to EM-UHMWPE/0.5.
The low-velocity impact behaviour of pineapple leaf fiber, PALF reinforce epoxy composite (P), PALF hybrid (GPG), and four-layer woven glass fiber (GGGG) composite was investigated. As for post-impact analysis, the damage evaluation was assessed through photographic images and X-ray computed tomography, using CT scan techniques. The key findings from this study are that a positive hybrid effect of PALF as a reinforcement was seen where the GPG shows the delayed time taken for damage initiation and propagation through the whole sample compared to GGGG. This clearly shows that the addition of fibers does have comparable composite properties with a fully synthetic composite. Through the visual inspection captured by photographic image, the presence of woven fiber glass mat in GPG presents a different damage mode compared to P. Moreover, CT scan results show extended internal damage at the cross-section of all impacted composite.
Food contamination leading to the spoilage and growth of undesirable bacteria, which can occur at any stage along the food chain, is a significant problem in the food industry. In the present work, biopolymer polybutylene succinate (PBS) and polybutylene succinate/tapioca starch (PBS/TPS) films incorporating Biomaster-silver (BM) and SANAFOR® (SAN) were prepared and tested as food packaging to improve the lifespan of fresh chicken breast fillets when kept in a chiller for seven days. The incorporation of BM and SAN into both films demonstrated antimicrobial activity and could prolong the storability of chicken breast fillets until day 7. However, PBS + SAN 2%, PBS/TPS + SAN 1%, and PBS/TPS + SAN 2% films showed the lowest microbial log growth. In quality assessment, incorporation of BM and SAN into both film types enhanced the quality of the chicken breast fillets. However, PBS + SAN 1% film showed the most notable enhancement of chicken breast fillet quality, as it minimized color variation, slowed pH increment, decreased weight loss, and decelerated the hardening process of the chicken breast fillets. Therefore, we suggest that the PBS + SAN and PBS/TPS + SAN films produced in this work have potential use as antimicrobial packaging in the future.
Adequate awareness of sustainable materials and eco-legislation have inspired researchers to identify alternative sustainable and green composites for synthetic fiber-reinforced polymer composites in the automotive and aircraft industries. This research focused on investigating the physical, mechanical, and morphological properties of different hybrid Cyrtostachys renda (CR)/kenaf fiber (K) (10C:0K, 7C:3K, 5C:5K, 3C:7K, 0C:10K) reinforced with 0.5 wt% MWCNT-phenolic composites. We incorporated 0.5 wt% of MWCNT into phenolic resin (powder) using a ball milling process for 25 h to achieve homogeneous distribution. The results revealed that CR fiber composites showed higher voids content (12.23%) than pure kenaf fiber composites (6.57%). CR fiber phenolic composite was more stable to the swelling tendency, resulting in the lowest percentage of swelling rate (4.11%) compared to kenaf composite (5.29%). The addition of kenaf fiber into CR composites had improved the tensile, flexural, and impact properties. The highest tensile and flexural properties were found for weight fraction of CR and kenaf fiber at 5C:5K (47.96 MPa) and 3C:7K (90.89 MPa) composites, respectively. In contrast, the highest impact properties were obtained for 0C:10K composites (9.56 kJ/m2). Based on the FE-SEM image, the CR fiber lumen was larger in comparison to kenaf fiber. The lumen of CR fiber was attributed to higher void and water absorption, lower mechanical properties compared to kenaf fiber. 5C:5K composite was selected as an optimal hybrid composite, based on the TOPSIS method. This hybrid composite can be used as an interior component (non-load-bearing structures) in the aviation and automotive sectors.
Natural fibers have emerged as a potential alternate to synthetic fibers, because of their excellent performance, biodegradability, renewability and sustainability. This research has focused on investigating the thermal, visco-elastic and fire-retardant properties of different hybrid Cytostachys Renda (CR)/kenaf fiber (K) (50/0; 35/ 15, 25/25, 15/ 35, 0/50)-reinforced MWCNT (multi-walled carbon nanotubes)-modified phenolic composites. The mass% of MWCNT-modified phenolic resin was maintained 50 mass% including 0.5 mass% of MWCNT. In order to achieve homogeneous dispersion ball milling process was employed to incorporate the MWCNT into phenolic resin (powder). Thermal results from thermogravimetric analysis and differential scanning calorimetric analysis revealed that the hybrid composites (35/15; 35 mass% CR and 15 mass% K) showed higher thermal stability among the composite samples. Visco-elastic results revealed that kenaf fiber-based MWCNT-modified composites (0/50; 0 mass% CR and 50 mass% K) exhibited higher storage and loss modulus due to high modulus kenaf fiber. Fire-retardant analysis (UL-94) showed that all the composite samples met H-B self-extinguishing rating and exhibited slow burning rate according to limiting oxygen index (LOI) test. However, (15/35; 15 mass% CR and 35 mass% K) hybrid composites showed the highest time to ignition, highest fire performance index, lowest total heat release rate, average mass loss rate, average fire growth rate index and maximum average rate of heat emission. Moreover, the smoke density of all hybrid composites was found to be less than 200 which meets the federal aviation regulations (FAR) 25.853d standard. Technique for Order Preference by Similarity to Ideal Solution (TOPSIS) was carried out to select an optimal composite sample considering the thermal, visco-elastic and fire-retardant behaviors. Through TOPSIS analysis, the hybrid (15/35; 15 mass% CR and 35 mass% K) composite sample has been selected as an optimal composite which can be used for high-temperature aircraft and automotive applications.
The aim of the present study has been to evaluate the effect of hybridization of montmorillonite (MMT) and multi-walled carbon nanotubes (MWCNT) on the thermal and viscoelastic properties of shape memory epoxy polymer (SMEP) nanocomposites. In this study, ultra-sonication was utilized to disperse 1%, 3%, and 5% MMT in combination with 0.5%, 1%, and 1.5% MWCNT into the epoxy system. The fabricated SMEP hybrid nanocomposites were characterized via differential scanning calorimetry, dynamic mechanical analysis, and thermogravimetric analysis. The storage modulus (E'), loss modulus (E"), tan δ, decomposition temperature, and decomposition rate, varied upon the addition of the fillers. Tan δ indicated a reduction of glass transition temperature (Tg) for all the hybrid SMEP nanocomposites. 3% MMT/1% MWCNT displayed best overall performance compared to other hybrid filler concentrations and indicated a better mechanical property compared to neat SMEP. These findings open a way to develop novel high-performance composites for various potential applications, such as morphing structures and actuators, as well as biomedical devices.
Polypyrrole (PPy) and polypyrrole/cerium oxide nanocomposite (PPy/CeO2) were prepared by the chemical oxidative method in an aqueous medium using anhydrous ferric chloride (FeCl3) as an oxidant. The successful formulation of materials was confirmed by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and transmittance electron microscopy (TEM). A four-in-line probe device was used for studying DC electrical conductivity and ammonia vapor sensing properties of PPy and PPy/CeO2. The significant improvement in both the conductivity and sensing parameters of PPy/CeO2 compared to pristine PPy reveals some synergistic/electronic interaction between PPy and cerium oxide nanoparticles (CeO2 NPs) working at molecular levels. The initial conductivity (i.e., conductivity at room temperature) was found to be 0.152 Scm-1 and 1.295 Scm-1 for PPy and PPy/CeO2, respectively. Also, PPy/CeO2 showed much better conductivity retention than pristine PPy under both the isothermal and cyclic ageing conditions. Ammonia vapor sensing was carried out at different concentration (0.01, 0.03, 0.05, 0.1, 0.2, 0.3, 0.4, and 0.5 vol %). The sensing response of PPy/CeO2 varied with varying concentrations. At 0.5 vol % ammonia concentration, the % sensing response of PPy and PPy/CeO2 sensor was found to be 39.1% and 93.4%, respectively. The sensing efficiency of the PPy/CeO2 sensor was also evaluated at 0.4. 0.3, 0.2, 0.1, 0.05, 0.03, and 0.01 vol % ammonia concentration in terms of % sensing response, response/recovery time, reversibility, selectivity as well as stability at room temperature.
The function of packaging is crucial in the maintenance of fresh meat product quality. This study aimed to assess the efficiency of six films added with coatings 2379L/220 and 2379L/221 (containing sage extracts) to inhibit Salmonella typhimurium, Staphylococcus aureus, and Escherichia coli, which showed that two of the six films had a significant effect. Additionally, the effects of the films on refrigerated skinless chicken breast meat were evaluated based on microbiological content, colour, weight loss, texture and pH. Four of the six films were examined could extend the storability of refrigerated chicken breast fillets for up to seven days. All six treated films improved the pH, colour stability, weight loss, and texture of the chicken fillets. Therefore, these findings suggested that the coatings containing sage extracts having different viscosities (2379L/220 and 2379L/221) were effective as antimicrobial adhesives in food packaging films and can be commercially applied in prolonging the storage of chicken breast meat without affecting their quality.