Flexural properties of poly(methyl methacrylate) resin reinforced with oil palm empty fruit bunch fibers: a preliminary finding

John J, Ann Mani S, Palaniswamy K, Ramanathan A, Razak AA

J Prosthodont, 2015 Apr;24(3):233-8.
PMID: 24976147 DOI: 10.1111/jopr.12191

PURPOSE: The purpose of this preliminary study was to evaluate the flexural properties of poly(methyl methacrylate) (PMMA) reinforced with oil palm empty fruit bunch (OPEFB) fiber.
MATERIALS AND METHODS: The flexural strength and flexural modulus of three OPEFB fiber-reinforced PMMA were compared with a conventional and a commercially available reinforced PMMA. The three test groups included OPEFB fibers of 0.5 mm thickness, 2.0 mm thickness, and OPEFB cellulose.
RESULTS: All test group specimens demonstrated improved flexural strength and flexural modulus over conventional PMMA. Reinforcement with OPEFB cellulose showed the highest mean flexural strength and flexural modulus, which were statistically significant when compared to the conventional and commercially reinforced PMMA used in this study. OPEFB fiber in the form of cellulose and 0.5 mm thickness fiber significantly improved flexural strength and flexural modulus of conventional PMMA resin. Further investigation on the properties of PMMA reinforced with OPEFB cellulose is warranted.
CONCLUSIONS: Natural OPEFB fibers, especially OPEFB in cellulose form, can be considered a viable alternative to existing commercially available synthetic fiber reinforced PMMA resin.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
Co-Adsorptive Removal of Creatinine and Urea by a Three-Component Dual-Layer Hollow Fiber Membrane

Zainol Abidin MN, Goh PS, Said N, Ismail AF, Othman MHD, Hasbullah H, et al.

ACS Appl Mater Interfaces, 2020 Jul 22;12(29):33276-33287.
PMID: 32589391 DOI: 10.1021/acsami.0c08947

The development of wearable artificial kidney demands an efficient dialysate recovery, which relies upon the adsorption process. This study proposes a solution to solve the problem of competitive adsorption between the uremic toxins by employing two adsorptive components in a membrane separation process. Dual-layer hollow fiber (DLHF) membranes, which are composed of a polysulfone (PSf)/activated carbon (AC) inner layer and a PSf/poly(methyl methacrylate) (PMMA) outer layer, were prepared for co-adsorptive removal of creatinine and urea from aqueous solution. The DLHF membranes were characterized in terms of morphological, physicochemical, water transport, and creatinine adsorption properties. The membrane was then subjected to an ultrafiltration adsorption study for performance evaluation. The incorporation of AC in membrane, as confirmed by microscopic and surface analyses, has improved the pure water flux up to 25.2 L/(m2 h). A membrane with optimum AC loading (9 wt %) demonstrated the highest maximum creatinine adsorption capacity (86.2 mg/g) based on the Langmuir adsorption isotherm model. In the ultrafiltration adsorption experiment, the membrane removed creatinine and urea with a combined average percent removal of 29.3%. Moreover, the membrane exhibited creatinine and urea uptake recoveries of 98.8 and 81.2%, respectively. The combined action of PMMA and AC in the PSf DLHF membrane has made the adsorption of multiple uremic toxins possible during dialysate recovery.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
Fulltext Rheological studies of PMMA-PVC based polymer blend electrolytes with LiTFSI as doping salt

Liew CW, Durairaj R, Ramesh S

PLoS One, 2014;9(7):e102815.
PMID: 25051241 DOI: 10.1371/journal.pone.0102815

In this research, two systems are studied. In the first system, the ratio of poly (methyl methacrylate) (PMMA) and poly (vinyl chloride) (PVC) is varied, whereas in the second system, the composition of PMMA-PVC polymer blends is varied with dopant salt, lithium bis (trifluoromethanesulfonyl) imide (LiTFSI) with a fixed ratio of 70 wt% of PMMA to 30 wt% of PVC. Oscillation tests such as amplitude sweep and frequency sweep are discussed in order to study the viscoelastic properties of samples. Elastic properties are much higher than viscous properties within the range in the amplitude sweep and oscillatory shear sweep studies. The crossover of G' and G'' is absent. Linear viscoelastic (LVE) range was further determined in order to perform the frequency sweep. However, the absence of viscous behavior in the frequency sweep indicates the solid-like characteristic within the frequency regime. The viscosity of all samples is found to decrease as shear rate increases.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
New bioactive glass-ceramic: synthesis and application in PMMA bone cement composites

Abd Samad H, Jaafar M, Othman R, Kawashita M, Abdul Razak NH

Biomed Mater Eng, 2011;21(4):247-58.
PMID: 22182792 DOI: 10.3233/BME-2011-0673

In present study, a new composition of glass-ceramic was synthesized based on the Na2O-CaO-SiO2-P2O5 glass system. Heat treatment of glass powder was carried out in 2 stages: 600 °C as the nucleation temperature and different temperature on crystallization at 850, 950 and 1000 °C. The glass-ceramic heat-treated at 950 °C was selected as bioactive filler in commercial PMMA bone cement; (PALACOS® LV) due to its ability to form 2 high crystallization phases in comparison with 850 and 1000 °C. The results of this newly glass-ceramic filled PMMA bone cement at 0-16 wt% of filler loading were compared with those of hydroxyapatite (HA). The effect of different filler loading on the setting properties was evaluated. The peak temperature during the polymerization of bone cement decreased when the liquid to powder (L/P) ratio was reduced. The setting time, however, did not show any trend when filler loading was increased. In contrast, dough time was observed to decrease with increased filler loading. Apatite morphology was observed on the surface of the glass-ceramic and selected cement after bioactivity test.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
FTIR studies of PVC/PMMA blend based polymer electrolytes

Ramesh S, Leen KH, Kumutha K, Arof AK

Spectrochim Acta A Mol Biomol Spectrosc, 2007 Apr;66(4-5):1237-42.
PMID: 16919998

The polymer electrolytes composing of the blend of polyvinyl chloride-polymethyl methacrylate (PVC/PMMA) with lithium triflate (LiCF3SO3) as salt, ethylene carbonate (EC) and dibutyl phthalate (DBP) as plasticizers and silica (SiO2) as the composite filler were prepared. FTIR studies confirm the complexation between PVC/PMMA blends. The CCl stretching mode at 834 cm-1 for pure PVC is shifted to 847 cm-1 in PVC-PMMA-LiCF3SO3 system. This suggests that there is interaction between Cl in PVC with Li+ ion from LiCF3SO3. The band due to OCH3 at 1150 cm-1 for PVC-PMMA blend is shifted to 1168 cm-1 in PVC-PMMA-LiCF3SO3 system. This shift is expected to be due to the interaction between Li+ ion and the oxygen atom in PMMA. The symmetric vibration band and the asymmetric vibration band of LiCF3SO3 at 1033 and 1256 cm-1 shifted to 1075 and 1286 cm-1 in the DBP-EC plasticized PVC-PMMA-LiCF3SO3 complexes. The interaction between Li+ ions and SiO2 will lead to an increase in the number of free plasticizers (which does not interact with Li+ ions). When the silica content increases from 2% to 5%, the intensity of the peak at 896 cm-1 (due to the ring breathing vibration of free EC) increases in PVC-PMMA-LiCF3SO3-DBP-EC system.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
FTIR spectra of plasticized grafted natural rubber-LiCF3SO3 electrolytes

Kumutha K, Alias Y

Spectrochim Acta A Mol Biomol Spectrosc, 2006 May 15;64(2):442-7.
PMID: 16530471

Chemical modification of natural rubber (NR) has frequently been attempted to improve the performance in specific application. 30% poly(methyl metacrylate) (PMMA) grafted into NR (MG30) has been explored as a potential candidate for polymer electrolytes. The complexation effect of salt and plasticizer in polymer host electrolytes had been investigated using FTIR. The carbonyl stretch of MG30 locates at 1729 cm-1, with the addition of lithium trimethanesulfonate (LiCF3SO3) salt, new band evolves at lower frequency region at 1643-1645 cm-1. The nondegenerate vibrational mode of nus(SO3) of salted electrolytes appearing at 1031-1034 cm-1 comes from 'free' trimethanesulfonate anions and the 1040-1046 cm-1 absorption from the monodentate ion paired with triflates. These indicate MG30-salt interaction. When MG30 and ethylene carbonate (EC) formed film, the CH3 asymmetric bend of MG30 appearing at 1447cm-1 is shifted to 1449 cm-1 in the EC-polymer complex. The CO stretching at 1729 cm-1 also shifted to 1728 cm-1. Hence, the EC-MG30 system is complexed to each other. EC-LiCF3SO3 interactions are indicated by the shifting of CO bending band of EC from 718 cm-1 being shifted to 720 cm-1 in the complex. In Li+-EC interaction where the ring breathing region at 897 cm-1 in EC has shifted to 899 cm-1 in EC-salt spectrum. The band appearing at 1643-1645 cm-1 due to the coordination of Li+

Matched MeSH terms: Polymethyl Methacrylate/chemistry
Some flexural properties of a nylon denture base polymer

Yunus N, Rashid AA, Azmi LL, Abu-Hassan MI

J Oral Rehabil, 2005 Jan;32(1):65-71.
PMID: 15634304

Nylon denture base material could be a useful alternative to poly (methyl methacrylate) (PMMA) in special circumstances such as patient allergy to the monomer. The aim of this study was to evaluate the flexural properties of a nylon denture base material (Lucitone FRS), a conventional compression-moulded heat-polymerized (Meliodent), a compression-moulded microwave-polymerized (Acron MC) and an injection-moulded microwave-polymerized (Lucitone 199) PMMA polymers. The effect of aldehyde-free, oxygen releasing disinfectant solution (Perform) on these properties was also investigated. The flexural modulus and the flexural strength were assessed with a three-point bending test. Specimens were stored in water at a temperature of 37 degrees C for 30 days. For each material, half of the prepared specimens were randomly selected and immersed in the disinfectant 24 h prior to testing. Results were compared statistically at a confidence level of 95%. The result showed that in both the control and disinfected groups, the flexural modulus of nylon was significantly lower than the three PMMA polymers. The flexural strength of nylon was significantly lower than those of Meliodent and Acron MC but was comparable with Lucitone 199. A 24-h immersion in the disinfecting solution increased the rigidity of nylon denture base material.

Matched MeSH terms: Polymethyl Methacrylate/chemistry
Synthesis and characterization of a new vertebroplasty cement based on gold-containing PMMA microspheres

Jacobs E, Saralidze K, Roth AK, de Jong JJ, van den Bergh JP, Lataster A, et al.

Biomaterials, 2016 Mar;82:60-70.
PMID: 26751820 DOI: 10.1016/j.biomaterials.2015.12.024

There are a number of drawbacks to incorporating large concentrations of barium sulfate (BaSO4) as the radiopacifier in PMMA-based bone cements for percutaneous vertebroplasty. These include adverse effects on injectability, viscosity profile, setting time, mechanical properties of the cement and bone resorption. We have synthesized a novel cement that is designed to address some of these drawbacks. Its powder includes PMMA microspheres in which gold particles are embedded and its monomer is the same as that used in commercial cements for vertebroplasty. In comparison to one such commercial cement brand, VertaPlex™, the new cement has longer doughing time, longer injection time, higher compressive strength, higher compressive modulus, and is superior in terms of cytotoxicity. For augmentation of fractured fresh-frozen cadaveric vertebral bodies (T6-L5) using simulated vertebroplasty, results for compressive strength and compressive stiffness of the construct and the percentage of the volume of the vertebral body filled by the cement were comparable for the two cements although the radiopacity of the new cement was significantly lower than that for VertaPlex™. The present results indicate that the new cement warrants further study.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
A practical three visit complete denture system

Ling BC

Ann R Australas Coll Dent Surg, 2000 Oct;15:66-8.
PMID: 11709981

Standard prosthodontic procedures require five visits to construct a set of complete maxillary and mandibular dentures. Various attempts have been made to reduce these procedures to four or three appointments. However, most of these techniques require the use of visible light polymerized resin as the final denture base materials. Visible light-cured resin materials have inferior physical properties and biocompatibility problems as compared with heat cured polymethylmethacrylate. This paper describes a system of complete denture construction which requires three clinical appointments instead of the usual five visits. This system is made possible by using the VLC base/tray material as the preliminary impression material as well as the application of a new biometric wax occlusion rim. It retains the use of polymethylmethacrylate as the denture base material. This system also utilizes all the procedures used in the conventional five appointment system of complete denture construction.

Matched MeSH terms: Polymethyl Methacrylate/chemistry
A three-visit, complete-denture technique utilizing visible light-cured resin for tray and base plate construction

Ling BC

Quintessence Int, 2004 Apr;35(4):294-8.
PMID: 15119715

This article describes a technique of constructing a set of maxillary and mandibular complete dentures in three visits instead of the usual five clinical appointments. This system of complete-denture construction is made possible because of the combined use of visible light-cured material as an impression tray and record base material, as well as the use of new biometric wax occlusion rims. Unlike some earlier techniques that use light-cured resin composites as the denture base materials, this method retains the use of heat-cured polymethylmethacrylate as the denture base material.

Matched MeSH terms: Polymethyl Methacrylate/chemistry
Studies on the effects of titanate and silane coupling agents on the performance of poly (methyl methacrylate)/barium titanate denture base nanocomposites

Elshereksi NW, Ghazali MJ, Muchtar A, Azhari CH

J Dent, 2017 Jan;56:121-132.
PMID: 27916635 DOI: 10.1016/j.jdent.2016.11.012

OBJECTIVES: This study aimed to fabricate and characterise silanated and titanated nanobarium titanate (NBT) filled poly(methyl methacrylate) (PMMA) denture base composites and to evaluate the behaviour of a titanate coupling agent (TCA) as an alternative coupling agent to silane. The effect of filler surface modification on fracture toughness was also studied.
METHODS: Silanated, titanated and pure NBT at 5% were incorporated in PMMA matrix. Neat PMMA matrix served as a control. NBT was sonicated in MMA prior to mixing with the PMMA. Curing was carried out using a water bath at 75°C for 1.5h and then at 100°C for 30min. NBT was characterised via Fourier transform-infrared spectroscopy (FTIR), Transmission Electron Microscopy (TEM) and Brunauer-Emmett-Teller (BET) analysis before and after surface modification. The porosity and fracture toughness of the PMMA nanocomposites (n=6, for each formulation and test) were also evaluated.
RESULTS: NBT was successfully functionalised by the coupling agents. The TCA exhibited the lowest percentage of porosity (0.09%), whereas silane revealed 0.53% porosity. Statistically significant differences in fracture toughness were observed among the fracture toughness values of the tested samples (p<0.05). While the fracture toughness of untreated samples was reduced by 8%, an enhancement of 25% was achieved after titanation. In addition, the fracture toughness of the titanated samples was higher than the silanated ones by 10%.
CONCLUSION: Formation of a monolayer on the surface of TCA enhanced the NBT dispersion, however agglomeration of silanated NBT was observed due to insufficient coverage of NBT surface. Such behaviour led to reducing the porosity level and improving fracture toughness of titanated NBT/PMMA composites. Thus, TCA seemed to be more effective than silane.
CLINICAL SIGNIFICANCE: Minimising the porosity level could have the potential to reduce fungus growth on denture base resin to be hygienically accepTable Such enhancements obtained with Ti-NBT could lead to promotion of the composites' longevity.

Matched MeSH terms: Polymethyl Methacrylate/chemistry*
Fulltext Methyl methacrylate cranioplasty

Azmi A, Latiff AZ, Johari A

Med J Malaysia, 2004 Aug;59(3):418-21.
PMID: 15727391

We conducted a prospective study in order to audit our experience of repairing cranial defects using Methyl methacrylate. This included a total of 49 patients undergoing cranioplasty using methyl methacrylate, of which 45 were males and 4 females. The age of patients at the time of surgery ranged from 16 to 40 years old, with an average of 24 years. Malays were the majority (67%), followed by Chinese (23%) and Indian (10%). Cranial defects were mainly caused by motor vehicle accident (94%), while gunshot wounds, industrial accidents and tumours, each contribute 2%. Bone flaps were commonly removed during previous surgery related to traumatic subdural haemorrhage (33%), contusion (21%) and intracerebral haemorrhage (14%). The size of cranial defects ranged from 28 cm2 to 440 cm2, with an average of 201 cm2. Most had right sided (55%) and lateral defects [temporoparietal (52%) followed by temporal (16%), frontal (16%), frontotemporal (14%) and occipital (2%)]. Duration of surgery ranged from 70 to 275 minutes, with an average of 135 minutes. Nine of 12 patients (75%) with neurological disability had some improvement while 85% of symptomatic patients had symptoms improvement after cranioplasty. The infection rate in this series was 4%.

Matched MeSH terms: Polymethyl Methacrylate/chemistry
Some mechanical properties of a highly cross-linked, microwave-polymerized, injection-molded denture base polymer

Memon MS, Yunus N, Razak AA

Int J Prosthodont, 2001 May-Jun;14(3):214-8.
PMID: 11484567

PURPOSE: The impact strength and the flexural properties of denture base materials are of importance in predicting their clinical performance upon sudden loading. This study compares the impact and transverse strengths and the flexural modulus of three denture base polymers.
MATERIALS AND METHODS: The investigation included a relatively new microwave-polymerized polyurethane-based denture material processed by an injection-molding technique, a conventional microwave-polymerized denture material, and a heat-polymerized compression-molded poly(methyl methacrylate) (PMMA) denture material. Impact strength was determined using a Charpy-type impact tester. The transverse strength and the flexural modulus were assessed with a three-point bending test. The results were subjected to statistical analysis using a one-way analysis of variance and the Scheffé test for comparison.
RESULTS: The impact strength of the microwave-polymerized injection-molded polymer was 6.3 kl/m2, while its flexural strength was 66.2 MPa. These values were lower than those shown by the two compression-molded PMMA-based polymers. The differences were statistically significant. The flexural modulus of the new denture material was 2,832 MPa, which was higher than the conventional heat-polymerized polymer but was comparable to the other microwave-polymerized PMMA-based polymer. The difference in the flexural modulus was statistically significant.
CONCLUSION: In terms of the impact and flexural strengths, the new microwave-polymerized, injection-molded, polyurethane-based polymer offered no advantage over the existing heat- and microwave-polymerized PMMA-based denture base polymers. However, it has a rigidity comparable to that of the microwave-polymerized PMMA polymer.

Matched MeSH terms: Polymethyl Methacrylate/chemistry