We test the feasibility of TiO2(B)@carbon composites as adsorbents, derived from wheat straws, for tetracycline (TC) adsorption from aqueous solutions. Hydrochar (HC), biochar (BC), and hydrochar-derived pyrolysis char (HDPC) are synthesized hydrothermally from the waste and then functionalized with TiO2(B), named as 'Composite-1', 'Composite-2', and 'Composite-3', respectively. A higher loading of TiO2(B) into the HC was also synthesized for comparison, named as 'Composite-4'. To compare their physico-chemical changes before and after surface modification, the composites are characterized using FESEM-EDS, XRD, BET, FRTEM, and FTIR. The effects of H2O2 addition on TC removal are investigated. Adsorption kinetics and isotherms of TC removal are studied, while TC adsorption mechanisms are elaborated. We found that the Composite-4 has the highest TC removal (93%) at pH 7, 1 g/L of dose, and 4 h of reaction time at 50 mg/L of TC after adding H2O2 (10 mM). The TC adsorption capacities of the Composite-1 and Composite-4 are 40.65 and 49.26 mg/g, respectively. The TC removal by the Composite-1 follows the pseudo-second order. Overall, this suggests that converting the wheat straw into HC and then functionalizing its surface with TiO2(B) as a composite has added values to the waste as an adsorbent for wastewater treatment.
Sugar molasses from agricultural waste could be a sustainable carbon source for the synthesis of graphene adsorbent introduced in this work. The sugar molasses was successfully converted to graphene-like material and subsequently coated on the sand as graphene sand composite (GSC), as proven by XRD, XPS, Raman spectroscopy, and SEM with EDX mapping analyses. The adsorption performance of GSC was evaluated against the removal of Tetracycline (TC) and methylene blue (MB) pollutants from an aqueous solution in a fixed bed column continuous-flow adsorption setup. The effect of different process conditions: bed height (4-12 cm), influent flow rate (3-7 mL/min), and contaminants' concentration (50-150 ppm) was investigated. The results revealed that column performance was improved by increasing the bed depth and lowering the flow rate and concentration of the pollutants. The best removal efficiency was obtained when the bed height was 12 cm, the influent flow rate of 3 mL/min, and the pollutants' initial concentration was 50 mg/L. Thomas, Adams-Bohart, and Yoon-Nelson models were attempted to fit the breakthrough curves. Regeneration of the GSC indicated the decline of breakthrough time from 240-280 to 180 min, reflecting the decrease in adsorptive sites due to the incomplete regeneration process. Overall, sugar molasses was shown to be a low-cost precursor for synthesizing valuable graphene material in the form of GSC, which can reduce the problem for industrial waste management of sugar molasses, and the GSC could be used as an adsorbent for environmental application.