The emission of waste anaesthetic gas is a growing contributor to global warming and remains a factor in atmospheric ozone depletion. Volatile anaesthetics in medical waste gases could be removed via adsorption using suitable activated carbon materials possessing an enhanced affinity to anaesthetic molecules. In this work, the effects of surface physical and chemical properties on sevoflurane adsorption were investigated by oxidative hydrothermal surface modification of a commercial activated carbon using only distilled water. The hydrothermal surface modification was carried out at different treatment temperatures (150-300 °C) for varying durations (10-30 min), and adsorption was conducted under fixed conditions (bed depth = 10 cm, inlet concentration = 528 mg/L, and flow rate = 3 L/min). The hydrothermal treatment generally increased the BET surface area of the activated carbons. At oxidation temperatures above 200 °C, the micropore volume of the samples diminished. The relative amount of surface oxygen was enriched as the treatment temperature increased. Treatment duration did not significantly affect the introduction of relative amount of surface oxygen, except at higher temperatures. There were no new types of functional groups introduced. However, disappearance and re-formation of oxygen functional groups containing C-O structures (as in hydroxyl and ether groups) occurred when treatment temperature was increased from 150 to 200 °C, and when treatments were conducted above 200 °C, respectively. The ester/acetal groups were enriched under the temperature range studied. The findings suggested that the re-formation of surface oxygen functionalities might lead to the development of functional groups that improve sevoflurane adsorption.
Activated carbons have been reported to be useful for adsorptive removal of the volatile anaesthetic sevoflurane from a vapour stream. The surface functionalities on activated carbons could be modified through aqueous oxidation using oxidising solutions to enhance the sevoflurane adsorption. In this study, an attempt to oxidise the surface of a commercial activated carbon to improve its adsorption capacity for sevoflurane was conducted using 6 mol/L nitric acid, 2 mol/L ammonium persulfate, and 30 wt per cent (wt%) of hydrogen peroxide (H2O2). The adsorption tests at fixed conditions (bed depth: 10 cm, inlet concentration: 528 mg/L, and flow rate: 3 L/min) revealed that H2O2 oxidation gave desirable sevoflurane adsorption (0.510 ± 0.005 mg/m2). A parametric study was conducted with H2O2 to investigate the effect of oxidation conditions to the changes in surface oxygen functionalities by varying the concentration, oxidation duration, and temperature, and the Conductor-like Screening Model for Real Solvents (COSMO-RS) was applied to predict the interactions between oxygen functionalities and sevoflurane. The H2O2 oxidation incorporated varying degrees of both surface oxygen functionalities with hydrogen bond (HB) acceptor and HB donor characters under the studied conditions. Oxidised samples with enriched oxygen functionalities with HB acceptor character and fewer HB donor character exhibited better adsorption capacity for sevoflurane. The presence of a high amount of oxygen functional groups with HB donor character adversely affected the sevoflurane adsorption despite the enrichment of oxygen functional groups with HB acceptor character that have a higher tendency to adsorb sevoflurane.
The inhalational anaesthetic agent - sevoflurane is widely employed for the induction and maintenance of surgical anaesthesia. Sevoflurane possesses a high global warming potential that imposes negative impact to the environment. The only way to resolve the issue is to remove sevoflurane from the medical waste gas before it reaches the atmosphere. A continuous adsorption study with a fixed-bed column was conducted using two commercial granular activated carbons (E-GAC and H-GAC), to selectively remove sevoflurane. The effect of bed depth (Z, 5-15 cm), gas flow rate (Q, 0.5-6.0 L/min) and inlet sevoflurane concentration (C0, ∼55-700 mg/L) was investigated. E-GAC demonstrated ∼60% higher adsorption capacity than H-GAC under the same operating conditions. Varying the levels of Z, Q and C0 showed significant differences in the adsorption capacities of E-GAC, whereas only changing the C0 level had significant differences for H-GAC. Three breakthrough models (Adams-Bohart, Thomas, and Yoon-Nelson) and Bed-depth/service time (BDST) analysis were applied to predict the breakthrough characteristics of the adsorption tests and determine the characteristic parameters of the column. The Yoon-Nelson and Thomas model-predicted breakthrough curves were in good agreement with the experimental values. In the case of the Adams-Bohart model, a low correlation was observed. The predicted breakthrough time (tb) based on kinetic constant (kBDST) in BDST analysis showed satisfactory agreement with the measured values. The results suggest the possibility of designing, scaling up and optimising an adsorption system for removing sevoflurane with the aid of the models and BDST analysis.