We had successfully synthesised Mg-doped zinc oxide (MZO) and Cudoped zinc oxide (CZO) nanorod arrays (NRAs) on Al-doped ZnO (ZAO)-coated glass substrates using immersion method and investigated their structural properties. With the incorporation of the Mg dopant, the length and crystallinity of MZO NRAs is higher compared to that of the CZO NRAs. The average optical transmittance of MZO NRAs was slightly lower than that of the CZO NRAs over the visible wavelength region. With the incorporation of the Cu dopant, the morphology of the CZO sample was slightly different from that of the MZO NRAs. The CZO NRAs present granular with small sphere shape. On the other hand, the MZO NRAs exhibit a hexagonal shape structure with a flat-top facet. Rods with a diameter of 58.9-96.7 nm were uniformly grown on the ZAO-coated glass substrate. This paper presents the growth behaviors of the MZO and CZO NRAs.
We report the use of a new precursor as active agents to promote the growth of carbon nanotubes (CNT) in methane ambient using a simple thermal chemical vapour deposition method. The agents consist of ammonia and methanol mixed at different ratios and was found to enhance the growth of CNTs. The optimum methanol to ammonia ratio was found to be 8 to 5, whereby longer and denser CNTs were produced compared to other ratios. The result was found otherwise when the experiment was done solely in methane ambient. In addition, CNT growth on substrates coated with double layer Ni catalyst was improved in terms of quality and density compared to a single coated substrates. This finding is supported by Raman spectrometry analysis.
Transparent nanostructured ZnO thin films were successfully deposited using sol-gel spin coating method on a quartz substrate. The 0.4 M ZnO solution gel was prepared using zinc acetate dihydrate (Zn(CH3COO)22H2O) as the precursor, 2-methoxyethanol as the solvent and monoethanolamine (MEA) as the stabilizer. The electrical and optical properties dependencies on the annealing temperature of the nanostructured ZnO thin films were investigated. It was found that as the annealing temperature increased, the particle size, conductivity and the peak of the UV emission also increased.
This paper addresses the growth of nano-structured MgZnO thin films by sol-gel spin coating method which will be used as a template layer to grow carbon nanotubes. The nano-structured MgZnO films were deposited on platinized (100) silicon substrates. In this work, we focused on the effect of aging and Mg content on the film structure and resistivity. Sols with Mg content of 10, 30 and 50 at.% were subjected to aging times of between 3 to 240 hours. Results from scanning (SEM) and field emission scanning electron (FESEM) microscopes and surface profiler (SP) showed that the sol aging increased the thickness, grain size and surface roughness for aging up to 240 hours. The energy dispersive analysis by X-ray (EDAX) confirmed the element of Mg in the ZnO films. The electrical resistivity also increased with aging time as confirmed by four point probe method. The results suggest that appropriate aging of the sol is important for improving physical quality and electrical performance of MgZnO thin films derived from sol-gel technique.
Zinc oxide (ZnO) is an emerging optoelectronic material in large area electronic applications due to its various functional behaviors. We present the fabrication and the characterization of ZnO nanorods. The ZnO nanorods were synthesized using sol-gel hydrothermal technique on oxidized silicon substrates. Different post-annealing temperatures were explored in the sol-gel hydrothermal synthesis of the ZnO nanorods. The surface morphology of the ZnO nanorods were examined using scanning electron microscope (SEM). In order to investigate the structural properties, the ZnO nanorods were measured using X-ray diffractometer (XRD). The optical properties were measured using ultraviolet-visible (UV-Vis) spectroscopy. The influence of the post-annealing temperature on the realized ZnO nanorods will be revealed and discussed in this paper.
Zinc oxide (ZnO) is an emerging material in large area electronic applications such as thin-film solar cells and transistors. We report on the fabrication and characterization of ZnO microstructures and nanostructures. The ZnO microstructures and nanostructures have been synthesized using sol-gel immerse technique on oxidized silicon substrates. Different precursor's concentrations ranging from 0.0001 M to 0.01 M (M=molarity) using zinc nitrate hexahydrate [Zn(NO3)2. 6H2O] and hexamethylenetetramine [C6H12N4] were employed in the synthesis of the ZnO structures. The surface morphologies were examined using scanning electron microscope (SEM) and atomic force microscope (AFM). In order to investigate the structural properties, the ZnO microstructures and nanostructures were measured using X-ray diffractometer (XRD). The optical properties of the ZnO structures were measured using photoluminescence (PL) and ultraviolet-visible (UV-Vis) spectroscopies.
In this work, nanocrystalline Ge1-xSnx alloy formation from a rapid thermal annealed Ge/Sn/Ge multilayer has been presented. The multilayer was magnetron sputtered onto the Silicon substrate. This was followed by annealing the layers by rapid thermal annealing, at temperatures of 300 °C, 350 °C, 400 °C, and 450 °C, for 10 s. Then, the effect of thermal annealing on the morphological, structural, and optical characteristics of the synthesized Ge1-xSnx alloys were investigated. The nanocrystalline Ge1-xSnx formation was revealed by high-resolution X-ray diffraction (HR-XRD) measurements, which showed the orientation of (111). Raman results showed that phonon intensities of the Ge-Ge vibrations were improved with an increase in the annealing temperature. The results evidently showed that raising the annealing temperature led to improvements in the crystalline quality of the layers. It was demonstrated that Ge-Sn solid-phase mixing had occurred at a low temperature of 400 °C, which led to the creation of a Ge1-xSnx alloy. In addition, spectral photo-responsivity of a fabricated Ge1-xSnx metal-semiconductor-metal (MSM) photodetector exhibited its extending wavelength into the near-infrared region (820 nm).
Gold nanoparticles (GNPs) are among the ideal nano-sized materials for medical applications such as imaging and drug delivery. Considering the significance of recent reports on acute phase induction of inflammatory mediators by GNPs, we studied the effect of GNPs on proinflammatory cytokines gene expression in mouse brain. Group 1 served as control whereas groups 2-4 were given only one intraperitoneal dose of 5, 20 and 50 nm GNPs, respectively and sacrificed after 24 h. The animals in groups 5-7 also received the same treatment but sacrificed after 7 days. Groups 8-10 received two injections of GNPs (5, 20 and 50 nm, respectively), first at the beginning of study and second on day 6, and sacrificed on day 7. Total RNA was extracted from the cerebral tissue and analyzed for the gene expressions of IL-1β, IL-6 and TNF-α. A single injection of 5 nm diameter GNPs significantly increased the mRNA expression of IL-1β and IL-6 in mouse brain on day 7, which was not augmented by the second dose of the same GNPs. Larger size GNPs (20 nm and 50 nm) did not cause any significant change in the expression of proinflammatory cytokines in mouse brain. In conclusion, systemic administration of small sized GNPs (5 nm) induced a proinflammatory cascade in mouse brain indicating a crucial role of GNPs size on immune response. It is important to use the right sized GNPs in order to avoid an acute phase inflammatory response that could be cytotoxic or interfere with the bioavailability of nanomaterials.