Recent developments in the transformation of biobased 5-hydroxymethylfurfural (HMF) into a potential liquid fuel, 2,5-dimethylfuran (DMF), are summarised. This review focuses briefly on the history of HMF conversion to DMF in terms of the feedstock used and emphasises the ideal requirements in terms of the catalytic properties needed in HMF transformation into DMF. The recent state of the art and works on HMF transformation into DMF are discussed in comparison to noble metals and non-noble metals as well as bimetallic catalysts. The effect of the support used and the reaction conditions are also discussed. The recommendations for future work and challenges faced are specified.
The aim of this work was to improve the processability of triglycidyl-p-aminophenol (TGPAP) epoxy resin. To achieve this improvement, a diluent, the diglycidyl ether of bisphenol F (DGEBF or BPF), was added to TGPAP, and the blended epoxy was then cured with 4, 4'-diaminodiphenyl sulfones (DDS). A response surface methodology (RSM) was used, with the target response being to achieve a blended resin with a high glass transition temperature (Tg) and maximum pot life (or processing window, PW). Characterization through dynamic mechanical thermal analysis (DMTA) and using a rheometer indicated that the optimum formulation was obtained at 55.6 wt.% of BPF and a stoichiometric ratio of 0.60. Both values were predicted to give Tg at 180 °C and a processing window of up to 136.1 min. The predicted values were verified, with the obtained Tg and processing window (PW) being 181.2 ± 0.8 °C and 140 min, respectively, which is close to the values predicted using the RSM.
Woven laminated composite has gained researchers' and industry's interest over time due to its impressive mechanical performance compared to unidirectional composites. Nevertheless, the mechanical properties of the woven laminated composite are hard to predict. There are many micromechanical models based on unidirectional composite but limited to the woven laminated composite. The current research work was conducted to evaluate elastic moduli of hybrid jute-ramie woven reinforced unsaturated polyester composites using micromechanical effectiveness unidirectional models, such as ROM, IROM, Halpin-Tsai, and Hirsch, which are based on stiffness. The hybrid jute-ramie laminated composite was fabricated with different layering sizes, and the stacking sequence was completed via hand lay-up with the compression machine. Tensile modulus values for hybrid composites are between those for single jute and single ramie. Obtained p-values less than 0.05 prove the relationship between layering size and tensile modulus. This study showed that several micromechanical models, such as Halpin-Tsai's predicted value of homogenized mechanical properties, were in good agreement with the experimental result. In the case of the hybrid composite, the micromechanical model deviates from the experimental result. Several modifications are required to improve the current existing model. A correlation function was calculated based on the differences between the elastic modulus values determined experimentally and those derived from each micromechanical model calculation.