Crude jatropha oil (JO) was modified to form jatropha oil-based polyol (JOL) via two steps in a chemical reaction known as epoxidation and hydroxylation. JOL was then reacted with isocyanates to produce JO-based polyurethane resin. In this study, two types of isocyanates, 2,4-toluene diisocyanate (2,4-TDI) and isophorone diisocyanate (IPDI) were introduced to produce JPUA-TDI and JPUA-IPDI respectively. 2,4-TDI is categorised as an aromatic isocyanate whilst IPDI is known as a cycloaliphatic isocyanate. Both JPUA-TDI and JPUA-IPDI were then end-capped by the acrylate functional group of 2-hydroxyethyl methacrylate (HEMA). The effects of that isocyanate structure were investigated for their physico, chemical and thermal properties. The changes of the functional groups during each synthesis step were monitored by FTIR analysis. The appearance of urethane peaks was observed at 1532 cm-1, 1718 cm-1 and 3369 cm-1 while acrylate peaks were detected at 815 cm-1 and 1663 cm-1 indicating that JPUA was successfully synthesised. It was found that the molar mass of JPUA-TDI was doubled compared to JPUA-IPDI. Each resin showed a similar degradation pattern analysed by thermal gravimetric analysis (TGA). For the mechanical properties, the JPUA-IPDI-based coating formulation exhibited a higher hardness value but poor adhesion compared to the JPUA-TDI-based coating formulation. Both types of jatropha-based polyurethane acrylate may potentially be used in an ultraviolet (UV) curing system specifically for clear coat surface applications to replace dependency on petroleum-based chemicals.
Four strains of bioflocculant-producing bacteria were isolated from a palm oil mill effluent (POME). The four bacterial strains were identified as Pseudomonas alcaliphila (B1), Pseudomonas oleovorans (B2), Pseudomonas chengduensis (B3), and Bacillus nitratireducens (B4) by molecular identification. Among the four bacterial strains, Bacillus nitratireducens (B4) achieved the highest flocculating activity (49.15%) towards kaolin clay suspension after eight hours of cultivation time and was selected for further studies. The optimum conditions for Eriochrome Black T (EBT) flocculation regarding initial pH, type of cation, and B4 dosage were determined to be pH 2, Ca2⁺ cations, and a dosage of 250 mL/L of nutrient broth containing B4. Under these conditions, above 90% of EBT dye removal was attained. Fourier transform infrared spectroscopic (FT-IR) analysis of the bioflocculant revealed the presence of hydroxyl, alkyl, carboxyl, and amino groups. This bioflocculant was demonstrated to possess a good flocculating activity, being a promissory, low-cost, harmless, and environmentally friendly alternative for the treatment of effluents contaminated with dyes.
Polychloropolymethylstyrene (PCMS) polymers were synthesized with clay Cloisite and without clay Cloisite and chloromethylstyrene (CMS) combine with styrene (1:1) v/v or known as copolymer and clay Cloisite by the polymerization process. The attenuated total reflection-Fourier transform infrared (ATR-FTIR) spectra of each polymer synthesized are reported. The spectra of IR shows the different value of the wavenumber and intensity for each set of different sample. The spectra can be as a reference for others to use in synthesizing this polymer and clay Cloisite for different type of application.
Soda lime silica (SLS) waste as the source of silica (SiO2) and ark clamshell (ACS) as the foaming agent has been utilized to fabricate the low-cost and lightweight foam glass-ceramics. A series of 1 and 6 wt% foam glass-ceramics were successfully prepared by the conventional solid-state sintering method at various sintering temperatures for 60 min. The bulk density of the samples has achieved minimum density (1.014 g/cm3) with maximum expansion (62.31%) at 6 wt% of the ACS content sintered at 800 °C for 60 min. The bulk density increases while the linear shrinkage and total porosity decrease with the progression of ACS contents and sintering temperature, where the results correspond with the FESEM micrograph. The result of XRD and FTIR transmittance spectra have shown that the formation of wollastonite crystal has occurred starting at 6 wt% of the ACS content sintered at 800 °C for 30 min. The highest mechanical performance (3.90 MPa) with an average total porosity (8.04%) is observed for the sample containing 1 wt% of ACS. It can be concluded that the composition of foam glass-ceramics (1 and 6 wt%) and sintering temperatures give significant results to the structural, physical, and mechanical properties of the fabricated foam glass-ceramics.
Agglomeration and restacking can reduce graphene oxide (GO) activity in a wide range of applications. Herein, GO was synthesized by a modified Hummer's method. To minimize restacking and agglomeration, in situ chemical oxidation polymerization was carried out to embed polyaniline (PANI) chains at the edges of GO sheets, to obtain GO-PANI nanocomposite. The GO-PANI was tested for the adsorptive removal of brilliant green (BG) from an aqueous solution through batch mode studies. Infrared (FT-IR) analysis revealed the dominance of hydroxyl and carboxylic functionalities over the GO-PANI surface. Solution pH-dependent BG uptake was observed, with maximum adsorption at pH 7, and attaining equilibrium in 30 min. The adsorption of BG onto GO-PANI was fit to the Langmuir isotherm, and pseudo-second-order kinetic models, with a maximum monolayer adsorption capacity (qm) of 142.8 mg/g. An endothermic adsorption process was observed. Mechanistically, π-π stacking interaction and electrostatic interaction played a critical role during BG adsorption on GO-PANI.
Biomass from oil palm frond leaves (OPFL) is an excellent reservoir of lignocellulosic material which full potential remains untapped. This study aimed to statistically optimize the covalent immobilization of Candida rugosa lipase (CRL) onto a ternary support comprised of OPFL derived nanocellulose (NC) and montmorillonite (MMT) in alginate (ALG) (CRL-ALG/NC/MMT). The coarser topology and the presence of characteristic spherical globules in the field emission scanning electron micrographs and atomic force micrographs, respectively, supported the existence of CRL on ALG/NC/MMT. In addition, amide peaks at 3478 and 1640 cm-1 in the fourier transform infrared spectra affirmed that CRL was covalently bonded to ALG/NC/MMT. The optimized Taguchi Design-assisted immobilization of CRL onto ALG/NC/MMT (7 h of immobilization, 35℃, pH 5, 7 mg/mL protein loading) gave a production yield of 92.89 % of ethyl levulinate (EL), as proven by gas chromatography-mass spectrometric ([M] +m/z 144, C7H12O3), FTIR and nuclear magnetic resonance (CAS-539-88-8) data. A higher optimal reaction temperature (50℃) and the reusability of CRL-ALG/NC/MMT for up to 9 esterification cycles substantiated the appreciable structural rigidification of the biocatalyst by ALG/NC/MMT, which improved the catalytic activity and thermal stability of the lipase.
In this work, fibrous silica-titania (FST) was successfully prepared by the microemulsion method prior to the addition of three types of carbonaceous materials: graphitic-carbon nitride, g-C3N4 (CN), graphene nanoplatelets (GN), and multi-wall carbon nanotubes, MWCNT (CNT), via a solid-state microwave irradiation technique. The catalysts were characterized using XRD, FESEM, TEM, FTIR, UV-Vis DRS, N2 adsorption-desorption, XPS and ESR, while their photoactivity was examined on the degradation of toxic 2-chlorophenol (2-CP). The result demonstrated that the initial reaction rate was in the following order: CNFST (5.1 × 10-3 mM min-1) > GNFST (2.5 × 10-3 mM min-1) > CNTFST (2.3 × 10-3 mM min-1). The best performance was due to the polymeric structure of g-C3N4 with a good dispersion of C and N on the surface FST. This dispersion contributed towards an appropriate quantity of defect sites, as a consequence of the greater interaction between g-C3N4 and the FST support, that led to narrowed of band gap energy (2.98 eV to 2.10 eV). The effect of scavenger and ESR studies confirmed that the photodegradation over CNFST occurred via a Z-scheme mechanism. It is noteworthy that the addition of green carbonaceous materials on the FST markedly enhanced the photodegradation of toxic 2-CP.
Photocatalysts provide excellent potential for the full removal of organic chemical pollutants as an environmentally friendly technology. It has been noted that under UV-visible light irradiation, nanostructured semiconductor metal oxides photocatalysts can degrade different organic pollutants. The Sn6SiO8/rGO nanocomposite was synthesized by a hydrothermal method. The Sn6SiO8 nanoparticles hexagonal phase was confirmed by XRD and functional groups were analyzed by FT-IR spectroscopy. The bandgap of Sn6SiO8 nanoparticles (NPs) and Sn6SiO8/GO composites were found to be 2.7 eV and 2.5 eV, respectively. SEM images of samples showed that the flakes like morphology. This Sn6SiO8/rGO nanocomposite was testing for photocatalytic dye degradation of MG under visible light illumination and excellent response for the catalysts. The enhancement of photocatalytic performance was mainly attributed to the increased light absorption, charge separation efficiency and specific surface area, proved by UV-vis DRS. Further, the radical trapping experiments revealed that holes (h+) and superoxide radicals (·O-₂) were the main active species for the degradation of MG, and a possible photocatalytic mechanism was discussed.
In this paper, the adsorptive performance of synthesized thiourea (TU) modified poly(acrylonitrile-co-acrylic acid) (TU-P(AN-co-AA)) polymeric adsorbent for capturing p-nitrophenol (PNP) from aqueous solution was investigated. TU-P(AN-co-AA) was synthesized via the redox polymerization method with acrylonitrile (AN) and acrylic acid (AA) as the monomers, then modified chemically with thiourea (TU). Characterization analysis with Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), elemental microanalysis for CHNS, zeta potential measurement, Brunauer-Emmett-Teller (BET) surface analysis and thermal analyses were carried out to determine the morphology and physico-chemical properties of the synthesized polymer. The characterization results indicated successful surface modification of polymer with TU. The performance of TU-P(AN-co-AA) for the removal of PNP was investigated under various experimental parameters (adsorbent dosage, initial adsorbate concentration, contact time and temperature). The results demonstrated that the Freundlich isotherm model and pseudo-second-order kinetic model best described the equilibrium and kinetic data, respectively. Thermodynamic studies showed that the uptake of PNP by TU-P(AN-co-AA) was spontaneous and exothermic in nature. The results of the regeneration studies suggested that the TU-P(AN-co-AA) polymer is a reusable adsorbent with great potential for removing PNP from wastewater.
The roles of multi-walled carbon nanotubes (MWNTs) and functionalised multiwalled carbon nanotubes (fMWNTs) in enhancing the efficacy of urea fertilizer (UF) as plant nutrition for local MR219 paddy variety was investigated. The MWNTs and fMWNTs were grafted onto UF to produce UF-MWNTs fertilizer with three different conditions, coded as FMU1 (0.6 wt. % fMWNTs), FMU2 (0.1 wt. % fMWNTs) and MU (0.6 wt. % MWNTs. The batches of MR219 paddy were systematically grown in accordance to the general practice performed by the Malaysian Agricultural Research and Development Institute (MARDI). The procedure was conducted using a pot under exposure to natural light at three different fertilization times; after a certain number of days of sowing (DAS) at 14, 35 and 55 days. Interestingly, it was found that the crop growth of plants treated with FMU1 and FMU2 significantly increased by 22.6% and 38.5% compared to plants with MU addition. Also, paddy treated with FMU1 produced 21.4% higher number of panicles and 35% more grain yield than MU while paddy treated with FMU2 gave 28.6% more number of panicles and 36% higher grain yield than MU, which implies the advantage of fMWNTs over MWNTs to be combined with UF as plant nutrition. The chemical composition and morphology of UF-MWNTs fertilizers which is further characterised by FTiR and FESEM confirmed the successful and homogeneous grafting of UF onto the fMWNTs.
Herein we reported the effect of doping and addition of surfactant on SnO2 nanostructures for enhanced photocatalytic activity. Pristine SnO2, Zn-SnO2 and SDS-(Zn-SnO2) was prepared via simple co-precipitation method and the product was annealed at 600 °C to obtain a clear phase. The structural, optical, vibrational, morphological characteristics of the synthesized SnO2, Zn-SnO2 and SDS-(Zn-SnO2) product were investigated. SnO2, Zn-SnO2 and SDS-(Zn-SnO2) possess crystallite size of 20 nm, 19 nm and 18 nm correspondingly with tetragonal structure and high purity. The metal oxygen vibrations were present in FT-IR spectra. The obtained bandgap energies of SnO2, Zn-SnO2 and SDS-(Zn-SnO2) were 3.58 eV, 3.51 eV and 2.81 eV due to the effect of dopant and surfactant. This narrowing of bandgap helped in the photocatalytic activity. The morphology of the pristine sample showed poor growth of nanostructures with high level of agglomeration which was effectively reduced for other two samples. Product photocatalytic action was tested beneath visible light of 300 W. SDS-(Zn-SnO2) nanostructure efficiency showed 90% degradation of RhB dye which is 2.5 times higher than pristine sample. Narrow bandgap, crystallite size, better growth of nanostructures paved the way for SDS-(Zn-SnO2) to degrade the toxic pollutant. The superior performance and individuality of SDS-(Zn-SnO2) will makes it a potential competitor on reducing toxic pollutants from wastewater in future research.
FTIR spectroscopy in combination with multivariate calibrations, i.e. partial least square (PLS) and principle component regression (PCR) was developed for quantitative analysis of cod liver oil (CLO) in binary mixture with corn oil (CO). The spectra of CLO, CO and their blends with certain concentrations were scanned using horizontal attenuated total reflectance (HATR) accessory at mid infrared (MIR) region of 4,000 – 650 cm-1. The optimal spectral treatments selected for calibration models were based on its ability to provide the highest values of coefficient of determination (R2) and the lowest values of root mean error of calibration (RMSEC). PLS was slightly well suited for quantitative analysis of CLO compared to PCR. FTIR spectroscopy in combination with multivariate calibration offers rapid, no excessive chemical reagent, and easy in operational to be applied for determination of CLO in binary mixture with other oils.
In this study, Li1+xAlxTi2-x(PO4)3 (0.0 ≤ x ≤ 0.5) was prepared by acetic acid-assisted sol-gel method. The structural properties of NASICON phosphates material with chemical formula LiTi2(PO4)3 were observed using the Fourier transform infrared spectroscopy. NASICON is a family of crystalline phosphate with a general network system consisting of PO4 tetrahedra, thus bands were assigned by vibrations contributed by basic phosphates, in the wavenumber region between 1300 cm-1 and 600 cm-1. Experimental spectra indicated that all Li1+xAlxTi2-x(PO4)3 (0.0 ≤ x ≤ 0.5), heat treated at 600°C and 700°C for 3 hours in air, samples showed the presence of phosphate peaks with shift in frequency as Al3+ is substituted into the structure, and with increasing temperatures. Some bands broadened and overlapped causing it hard to analyze the arising bands. It however determined the existence of NASICON structure in all of the samples under study.
This aim of this research is to investigate thermal stability of virgin coconut oil, (VCO) which was heated at 190°C upon 40 days storage as compared to extra virgin olive oil (EVOO). The changes in fatty acids composition through (GC), Fourier Transform Infrared (FTIR) spectra, iodine value (IV) and total phenolic content were determined throughout the period of study. Results from GC showed that there was significant changes (P
The aim of this work is to study the effect of hydrocolloids (guar gum, xanthan gum and carboxymethyl cellulose (CMC) on the physical properties and sensory evaluation of ice cream produced in order to investigate the potential of applying fermented glutinous rice (tapai pulut) as a value-added ingredient. The addition of 25% fermented glutinous rice was the most reliable amount to enhance the physical and sensory properties of ice cream when incorporating hydrocolloids. The addition of hydrocolloids significantly (p < 0.05) increased the pH, firmness, overrun, and melting rate of fermented glutinous rice ice cream. The addition of guar gum scored the highest firmness value (5403 g) followed by CMC (4630 g) and xanthan gum (3481g). Fermented glutinous rice ice cream with xanthan gum added, induced a noticeable change in overrun value (62%) while the addition of CMC decreased the melting rate compared to the control. The FTIR spectrum of fermented glutinous rice ice cream with different hydrocolloids containing carboxyl, amide and carbonyl group was appeared at 3362-3379 cm-1 , 1639-1640 cm-1 and 1026-1064 cm-1, respectively. In conclusion, the addition of xanthan gum presented great potential to improve the quality of fermented glutinous rice ice cream produced in terms of its firmness, overrun and melting rate.
A biodegradable composite (PLA/KBF blends) was prepared using melt blending technique in a brabender mixer and characterized with FTIR and TGA analyzer. Five percent of triacetin and glycerol contents were used as plasticizers to plasticise PLA matrix. KBF was treated with 4% NaOH solution, while 30 wt% of fibre loading was used constantly for all the composite samples. From the FTIR analysis, the additions of triacetin and glycerol to PLA composites did not produce any significant difference, and there were no chemical changes in both the plasticized PLA with the treated and untreated KBF, respectively. Observation done on the TGA analysis revealed that both plasticizers did improve the thermal stability of the composites, and this might be due to the modification on the fibre surfaces, which further led to the delay in the degradation of the PLA matrix and to significant stabilization effect.
This study demonstrated the utilization of radiation-induced initiator methods for the formation of
nanoparticles of Acrylated Palm Oil (APO) using aqueous Pluronic F-127 (PF-127) microemulsion
system. This microemulsion system was subjected to gamma irradiation to form the crosslinked APO
nanoparticles. Dynamic light scattering (DLS), Fourier Transform Infrared (FTIR) spectroscopy and
Transmission Electron Microscopy (TEM) were used to characterize the size and the chemical structure
of the nanoparticles. As a result, the size of the APO nanoparticle was decreased when the irradiation
dose increased. The decrease in size might be due to the effects of intermolecular crosslinking and
intramolecular crosslinking reactions of the APO nanoparticles during irradiation process. The size of the
nanoparticle is in the range of 98 to 200 nanometer (nm) after irradiation using gamma irradiator. This radiation-induced method provides a free initiator
induced and easy to control process as compared
to the classical or chemical initiator process. The
study has shown that radiation-induced initiator
methods, namely, polymerization and crosslinking
in the microemulsion, were promising for the
synthesis of nanoparticles.
Starch is a biodegradable polymer produced in abundance from many renewable resources. This study examined the influence of citric acid (0-40% w/wt%) ) and water (0-40% w/wt%) as secondary additive and glycerol as plasticizer on the mechanical properties of bio-plastic starch (BPS) from Malaysian sago. The CA content varies from 0 to 40 w/wt% while water was also varied from 0 to 40 w/wt%. FT-IR spectroscopy showed that acid citric improve the properties of BPS and water give negative effects to the carbon hydrogenbond. It is obvious that the addition of the CA at 30 wt/wt% improve the mechanical property of BPS to more than 40% compare to the addition of water.
The use of Fourier transform infrared (FTIR) spectroscopy coupled with chemometric techniques to differentiate butter from beef fat (BF) was investigated. The spectral bands associated with butter, BF, and their mixtures were scanned, interpreted, and identified by relating them to those spectroscopically representative to pure butter and BF. For quantitative analysis, partial least square (PLS) regression was used to develop a calibration model at the selected fingerprint regions of 1500-1000 cm-1, with the values of coefficient of determination (R2) and root mean square error of calibration (RMSEC) are 0.999 and 0.89% (v/v), respectively. The PLS calibration model was subsequently used for the prediction of independent samples containing butter in the binary mixtures with BF. Using 6 principal components, root mean square error of prediction (RMSEP) is 2.42% (v/v). These results proved that FTIR spectroscopy in combination with multivariate calibration can be used for the detection and quantification of BF in butter formulation for authentication use.
Mechanical properties of blended polyethylene (PE) containing the antioxidant Irganox 1010 and the UV-absorber Tinuvin 326 were studied for future use as radiation capsule material for the TRIGA Mark II research reactor. High density and low density polyethylene were blended with the additives and tested for elongation at break, impact strength and gel content, before and after irradiation inside the nuclear reactor. Characterization via FTIR as well as determination of crystallization and melt transition temperatures through DSC were also conducted. It was found that the addition of the antioxidant at different amounts (from 0 to 4 phr) had various effects on the properties of the blended PE, with 0 phr being the amount at which there was the biggest increase in elongation at break and impact strength, post-irradiation.