PURPOSE: The purpose of this bibliometric study was to analyze the characteristics of the Journal of Prosthetic Dentistry between 1970 and 2019.

MATERIAL AND METHODS: The Web of Science Core Collection was used to retrieve 9 categories of the Journal of Prosthetic Dentistry, including keywords and terms used, cited documents published, the countries and organizations of the authors, references, and sources cited during this period. Data were exported to a software program and analyzed for each 10-year period and for the entire 50 years. The highest 10 in each category were reported. Co-occurrence, couthorships, and linkage were also reported.

RESULTS: A total of 11 989 records were reached by the search on the Web of Science Core Collection database; of which, 10 638 (92.9%) were included in the analysis. Articles made up 91.1%, of all records, with 217 review documents (1.8%). The most productive decade was 1980 to 1989 with 2936 documents. The total number of citations of all documents (available period 1980 to 2019) including self-citations was 155 112. During the period 1970 to 2019, 14 837 terms were used. The total number of keywords was 4933 (available period 1990 to 2019). There were 15 382 authors, 82 countries, and 2113 organizations identified in articles published in the Journal of Prosthetic Dentistry during this period, with most from the United States. There were 43 027 authors, 95 324 references, and 14 594 sources cited in the Journal of Prosthetic Dentistry during the period surveyed.

AIM: To evaluate the shear bond strength of Zinc phosphate cement Elite, glass ionomer cement Fuji I, resin-modified glass ionomer cement Fuji Plus and resin luting cement Panavia-F to Turkom-Cera all-ceramic material.

MATERIALS AND METHODS: Turkom-Cera was used to form discs 10mm in diameter and 3 mm in thickness (n = 40). The ceramic discs were wet ground, air - particle abraded with 50 - μm aluminium oxide particles and randomly divided into four groups (n = 10). The luting cement was bonded to Turkom-Cera discs as per manufacturer instructions. The shear bond strengths were determined using the universal testing machine at a crosshead speed of 0.5 mm/min. The data were analysed using the tests One Way ANOVA, the nonparametric Kruskal - Wallis test and Mann - Whitney Post hoc test.

RESULTS: The shear bond strength of the Elite, Fuji I, Fuji Plus and Panavia F groups were: 0.92 ± 0.42, 2.04 ± 0.78, 4.37 ± 1.18, and 16.42 ± 3.38 MPa, respectively. There was the statistically significant difference between the four luting cement tested (p < 0.05).

MATERIALS AND METHODS: Forty Turkom-Cera ceramic disks (10 mm × 3 mm) were prepared and randomly divided into four groups. The disks were wet ground to 1000-grit and subjected to four surface treatments: (1) No treatment (Control), (2) sandblasting, (3) silane application, and (4) sandblasting + silane. The four groups of 10 specimens each were bonded with Panavia-F resin cement according to manufacturer's recommendations. The SBS was determined using the universal testing machine (Instron) at 0.5 mm/min crosshead speed. Failure modes were recorded and a qualitative micromorphologic examination of different surface treatments was performed. The data were analyzed using the one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests.

RESULTS: The SBS of the control, sandblasting, silane, and sandblasting + silane groups were: 10.8 ± 1.5, 16.4 ± 3.4, 16.2 ± 2.5, and 19.1 ± 2.4 MPa respectively. According to the Tukey HSD test, only the mean SBS of the control group was significantly different from the other three groups. There was no significant difference between sandblasting, silane, and sandblasting + silane groups.

CONCLUSION: In this study, the three surface treatments used improved the bond strength of resin cement to Turkom-Cera disks.